采用晶体取向分布函数(ODF)研究和分析了中间退火对高纯铝箔立方织构的影响。研究结果表明:中间退火对高纯铝箔冷轧形变织构影响不大,但对成品退火箔材中立方织构和R织构含量产生重要影响,在300℃/2h中间退火条件下,成品箔材中再结晶立方织构取向密度最大,R织构含量较小。

The effect of middle annealing on cube texture of high-purity aluminum foils was investigated by means of orientation distribution functions (ODFs). The results show that the deformation textures except the Cu component were rarely affected by the middle annealing temperatures. But it bring about strong influence on the cube texture of aluminum foils after the final annealing. The cube texture is decreased as the middle annealing temperature is increased, while the R component is changed a little. The cube texture is the strongest in the middle annealing at 300℃/2h.

参考文献

[1] J Hasenclever;G Scharf.Evolution of Microstructure and Texture in Al 99/99-foils for High Voltage Electrolytic Capacitors[C][A].Grenoble,France,1996:565.
[2] ALDons;E Nes .Nucleationofcubetextureinaluminum[J].Materials Science and Technology,1986,2:8.
[3] O.Engler;M.-Y.Huh .Evolution of the cube texture in high purity aluminum capacitor foils by continuous recrystallization and subsequent grain growth[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,1999(1/2):371-381.
[4] TSuzuki;K Arai;M Shiga et al.Impurityeffectoncubetextureinaluminumfoils[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,1985,16:27.
[5] HJunge.Mathematischa Methoden der Textur Analyse[M].AkademieVerlag;Berlin,1969
[6] 毛卫民;Z Xin-ming(张新明).Quantitative Texture Analysis of Crystalline Materials晶体材料织构定量分析[M].北京:冶金工业出版社,1995
[7] KIto;K Lücke;R Rixen .Theinfluenceofpre-annealingandannealingtemperaturesontherecrystallizationtexturesofcoldrolledaluminium-ironalloys[J].Zeitschrift fur Metallkunde,1976,67(05):338.
[8] KIto et al.Theinfluenceofironcontentandannealingtemperatureontherecrystallizationtexturesofhigh-puriyaluminium-ironalloys[J].Acta Materialia,1983,31(12):2137.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%