研究了Ni3Al/ Ni7Hf2定向共晶复合材料的组织和凝固行为。结果表明， Ni- 5.8Al-32Hf 和 Ni-4Al-26Hf-8Cr-4W 合金是这类Ni3Al/ Ni7Hf2定向共晶复合材料的合适成分。这两种合金在铸态下存在Ni3Al和Ni7Hf2相。缓慢凝固时会出现少量β-NiAl相。三元合金和五元合金的凝固范围分别为41℃和57℃，临界G/R值分别为5×105和7×106℃*s*cm－2 。对三元合金在温度梯度G=250℃*cm－1 和生长速率R=5μm*s－1，对五元合金在G=350℃ cm－1和R=1μm*s－1 条件下制备了平行于生长方向定向排列Ni3Al/Ni7Hf2片状共晶材料。
参考文献
| [1] | Drapier J M.Progress in Advanced Directionally Solidified and Eutectic High Temperature Alloys[A].London: Applied Science Publishers Ltd,1978:701-726. |
| [2] | Neff M A;Rickinson B A et al.The Growth and Morphology of Directionally Solidified Nickel Base γ/γ′-δ Superalloys[J].Metallurgical and Materials Transactions,1978,9:469-476. |
| [3] | Lemkey F D.Solidification Technology. Proceeding of the First Army Materials Technology Conference[A].,1972:165-186. |
| [4] | 马书伟,郑运荣,于熙泓.Al量对Ni-Al-Hf-Cr-W系合金显微组织结构的影响[J].航空学报,1997(04):439. |
| [5] | Mclean M;Schubert F.Mechanical Properties of Directionally Solidified Alloys and Eutectic Composites[A].London: Applied Science Publishers Ltd,1978 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%