研究了Si2ON2/LAS纳米复合材料的制备和性能。结果表明，纳米β-Si3N4可在较低温度下与玻璃热压烧结制备出Si2ON2/LAS纳米复合材料。材料的力学性能与生成的纳米 Si2O N2含量有关。Si2ON2的含量在20％时材料的抗弯强度和断裂韧性达最高值，分别比未加 Si2 ON2的材料提高31％和88％。纳米Si2ON2的含量超过20％时，材料的力学性能急剧下降，其原因是材料的致密度迅速降低。
参考文献
| [1] | Karch J;Birringer R;Gleiter H .Ceramics ductile at low tempera ture[J].NATURE,1987,330(10):556. |
| [2] | 陈大明 .纳米陶瓷复合材料的制备与性能[J].材料导报,1997,11(05):67. |
| [3] | Lei Tian.SiC-nanoparticle-reinforced Si3N4 matrix composite[J].Journal of Materials Science,1998:797-802. |
| [4] | 王宏志;高濂 等.晶内型Al2O3-SiC纳米复合陶瓷的制备[J].无机材料学报,1997,12(05):671-674. |
| [5] | John Brennan;Karlm M Prewo.Silicon carbide fibre reinforced glass-ceramic matrix composite exhibiting high strength and toughness[J].Journal of Materials Science,1982(17):2371-2383. |
| [6] | Malcom E Washburn .Silicon Oxynitride Refractories[J].Ceramic Bulletin,1967,46(07):67-671. |
| [7] | Markus Bruno;Jan L.Holm .Thsting of Si_2ON_2-ceramics made from microsilica and Si_3N_4- powder[J].Key engineering materials,1997(3):1649-1652. |
| [8] | P W麦克米伦.微晶玻璃[M].北京:中国建筑工业出版社,1988 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%