用单辊熔体激冷法制得Al65Si35 (原子分数/%,下同)的铝硅合金薄带,厚度为0.02~0.03mm,宽度2mm.经过透射电子显微分析、能谱分析和X射线衍射分析.结果表明该合金的组织结构由纳米Si相、fcc-Al纳米颗粒及非晶相组成.形成了纳米/非晶复合材料.合金的显微硬度达到HV230.
参考文献
[1] | A Inoue;K Ohtera;T Masumoto .[J].Japanese Journal of Applied Physics,1988,27:1479. |
[2] | M Watanabe;A Inoue;H M Kimura;T Aiba,T Masumoto .[J].Materials Transactions,1993,34:162. |
[3] | A Tokar;L Levin .[J].Zeitschrift fur Metallkunde,1998,89:16. |
[4] | A. Gebert .Effect of oxygen on phase formation and thermal stability of slowly cooled Zr65Al7.5Cu17.5Ni10 metallic glass[J].Acta materialia,1998(15):5475-5482. |
[5] | G J Fan;W L ser;S RothJ Eckert .[J].Acta Materialia,2000,48:3823. |
[6] | F. YE;K. LU .PRESSURE EFFECT ON CRYSTALLIZATION KINETICS OF AN AI-La-Ni AMORPHOUS ALLOY[J].Acta materialia,1999(8):2449-2454. |
[7] | F Schurack;J Eckert;L Schultz.[J].Materials Science and Engineering,2000:164. |
[8] | F. SCHURACK;J. ECKERT;L. SCHULTZ .SYNTHESIS AND MECHANICAL PROPERTIES OF CAST QUASICRYSTAL-REINFORCED Al-ALLOYS[J].Acta materialia,2001(8):1351-1361. |
[9] | Q Jiang .[J].ZEITSCHRIFT FUR METALLKUNDE,2000,99:97. |
[10] | Y H Kim .A Inoue and T Masumoto[J].MATERIALS TRANSACTIONS,1991,32:7. |
[11] | T Egami;Y Waseda .[J].Journal of Non-Crystalline Solids,1984,64:113. |
[12] | HYZhang .[J].Journal of Physics:Condensed Matter,1995,7:5237. |
[13] | D Tabor.The Hardness of Metals[M].London:Oxford University Press,1951 |
[14] | R Hill.The Mathematical Theory of Plasticity[M].London:Oxford University Press,1967:213. |
[15] | A Inoue;Y Horio;Y H KimT Masumoto .[J].Materials Transactions,1992,33:669. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%