在GH536高温合金基材上,采用矩形积分透镜,激光重熔等离子喷涂NiCrAlY/8YSZ热障涂层.1050℃的静态氧化试验和热震试验的结果表明:激光重熔可以改善热障涂层的抗氧化性能,能量密度33J*mm-2的激光重熔试样具有高于等离子喷涂试样的热震寿命,氧化阻力的改善与重熔层致密组织有关,微细网状裂纹释放热震应力的作用是热震寿命提高的主要原因.
参考文献
[1] | H L Tsai;P C Tsai .[J].Materials Science and Engineering,1994,A177:227-232. |
[2] | H L Tsai;P C Tsai .[J].Surface and Coatings Technology,1995,71:53-59. |
[3] | H L Tsai;P C Tsai.[J].Journal of Materials Engineering and Performance,1995(04):689-696. |
[4] | R Sivacumar;B L Mordike .[J].Surface Engineering,1988,4(02):127-140. |
[5] | I Zaplatynsy .[J].THIN SOLID FILMS,1982,95:273-284. |
[6] | K C Chang;W J Wei;C Chen .[J].Surface and Coatings Technology,1998,102:197-204. |
[7] | L Lelait;S Alperine;R Mevrel .[J].Journal of Materials Science,1992,27:5-12. |
[8] | K M Jasim;R D Dawtings;D R F West .[J].Materials Science and Technology,1992,8:83-91. |
[9] | M. Leoni;R. L. Jones;P. Scardi .Phase stability of scandia-yttria-stabilized zirconia TBCs[J].Surface & Coatings Technology,1998(1/3):107-113. |
[10] | S V Joshi;M P Srivastava .[J].SURFACE ENGINEERING,1995,11(03):233-239. |
[11] | B C Wu;E Chang .[J].Journal of the American Ceramic Society,1989,72(02):212-218. |
[12] | R A Miller .[J].Journal of the American Ceramic Society,1984,67(08):517-521. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%