针对C*参数的不足,本研究修正Q*并得到了一个新的蠕变裂纹扩展速率(CCGR)控制参数Q*(t).该参数综合了温度、应力场、激活能等影响因素,很好地表征了在不同应力或温度条件下蠕变裂纹扩展的特性.该参数能完整关联整个蠕变裂纹扩展的不同阶段,并从材料蠕变断裂的机制上反映了蠕变裂纹扩展的本质.
参考文献
[1] | YOKOBORI A T et al.An alternative correlating parameter for creep crack growth rate and its application:derivation of the parameterQ*[J].Materials at High Temperatures,1992,10(02):108-118. |
[2] | Kaji Y .Estimation of creep fracture life for Hastelloy XR by Q*parameter[J].Engineering Fracture Mechanics,1995,50:519-528. |
[3] | Yoshiyuki Kaji;Manfred Rodig;Kenji Kikuchi .Comparison and evaluation of creep crack growth rate and fracture time for alloy 800 by the Q parameter[J].International Journal of Pressure Vessels and Piping,1998(15):1065-1074. |
[4] | Yokobori T .Studies on crack growth rate under high temperature:Creep,fatigue and creep-fatigue interaction (I)[J].Engineering Fracture Mechanics,1980(13):509-522. |