研究了纯镍及其表面磁控溅射Ni-0.5Y微晶涂层在1000C空气中的恒温氧化和循环氧化行为.通过扫描电镜(SEM)和透射电镜(TEM)对涂层以及表面NiO氧化膜的形貌和结构进行了研究.此外,还用激光拉曼(Raman)谱对两种样品表面NiO氧化膜内应力大小进行了测量.结果表明,Ni-0.5Y微晶涂层与基体镍相比有更低的氧化增重速率,表面NiO氧化膜的晶粒尺寸明显减小,膜的高温塑性得以改善.同时,氧化膜内的压应力水平也有所降低,因而改善了NiO氧化膜的粘附性和保护性.磁控溅射涂层的微晶结构以及稀土元素钇的存在均有助于提高涂层的抗高温氧化性能.
参考文献
| [1] | H E Evans .Condition for initiation of oxide scale cracking and spallation[J].Corrosion Science,1984,24(01):209-216. |
| [2] | A G Evans .Stress and decohesion of oxide scales[J].Materials Science Forum,1989,43(03):243-249. |
| [3] | Y F Zhang .Spallation of oxide scales formed on Ni-30Cr alloy[J].Oxidation of Metals,1993,40(03):529-536. |
| [4] | J Birnie .Ex situ and in situ determination of stress distributions in chromium oxide films by Raman microscopy[J].Corrosion Science,1992,33(02):1-6. |
| [5] | HMJin .Influence of yttrium implantation on oxidation behavior of Co-40Cr alloy[J].稀土学报(英文版),1999,17(01):34-38. |
| [6] | 靳惠明,张林楠,李美栓,李铁藩.Rare Earth Effects on Adhesion of Cr2O3 Oxide Scale |
| [7] | 孙晓东;王佩璇 .离子注入纯铁表面微观结构研究[J].材料科学与工程,1997,15(02):45-49. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%