对近年来钛合金的缺陷、损伤及其预防与控制技术进行总结与归纳.结果表明,钛合金的常见缺陷可从与熔炼工艺有关的缺陷、与其它工艺相关的缺陷以及与表面完整性相关的缺陷三个方面进行分析;钛合金Ti3Al(α2)相的析出具有力学行为相关性;钛合金表面的氧化污染区包括氧高度污染区、氧化膜区、氧高梯度扩散区和氧缓慢扩散区,富氧层具有明显的缺口效应;采用断口定量分析技术可反推钛合金构件疲劳应力,且误差较小.
参考文献
[1] | Parkinson F L .SST Technology follow on program, phase I beta processes titanium alloy 6A1-4V plate[R].Boeing Co Seattle Wash Commercial Airplane Group. Report No: 60200 |
[2] | Brown B F .Titanium eliminates corrosion in nitric acid storage tanks[J].Met Rev Journal,1968,13:17-19. |
[3] | 陶春虎;刘庆琼;曹春晓.航空用钛合金的失效及其预防[M].北京:国防工业出版社,2002:114. |
[4] | M. L. Wasz;F. R. Brotzen;R. B. McLellan;A. J. Griffin Jr .Effect of oxygen and hydrogen on mechanical properties of commercial purity titanium[J].International Materials Reviews,1996(1):1-12. |
[5] | 马济民;朱知寿;蔡建明 .钛合金α斑点的研究[J].金属学报,1999,35(01):445. |
[6] | Gu J L;Zhu Z S;Chen N P.Phase transformation textures in cole rolled and annealed titanium sheets[A].北京,1996:622. |
[7] | ZHANG S Q;Tao C H;Yan M G .The effect of various microstructures on low cycle fatigue behavior in TC6 titanium alloy[R].ASTM STP942,1988. |
[8] | Tao C H;Zhang S Q;Yan M G.An investigation on the mechanism of fatigue crack propagation in various microstructures for a TC6 titanium alloy[A].北京,1987:629-633. |
[9] | 赵爱国;史亦伟;张卫方.两批钛合金棒材的特性对比研究[J].材料工程 |
[10] | 蒲正利;王克光;杨雄光 .TA1、TC4管材表面上的钨夹杂及脆裂[J].金属学报,1999,35(01):742. |
[11] | 赵永庆,朱康英,李左臣.Ti811合金的热稳定性能[J].稀有金属材料与工程,1997(03):35-39. |
[12] | Zhang W F;Xi N S;Wang L Y .Low pressure explosion analysis of a spherical gas-bottle made of titanium alloy[J].Engineering Failure Analysis,2002,9(03):329-334. |
[13] | 陶春虎,习年生,张卫方,钟培道.钛合金球形气瓶低压爆破分析及安全评估[J].机械工程材料,2000(06):32-35. |
[14] | Tao C H;Zhang S Q and Yan M G .Ti3Al phase precipitation during vibration loading for a titanium alloy[J].Trans of Nonferrous Metals Society of China,1995,5(02):71-75. |
[15] | Tao C H;Zhang S Q;Yan M G.Fatigue behavior and Ti3Al phase precipitation during vibration loading for a titanium alloy[A].Xi′an,1994:318-322. |
[16] | Gray G T.The effect of oxygen content on the fatigue crack propagation of Ti-8. 6Al[J].Titanium Science and Technology,1985(04):2115. |
[17] | Xu Y B;Xu Z S .Segregation of interstitial element and brittleness in Ti-6Al-4V[J].Journal of Materials Science,1990,25(09):3976. |
[18] | 张卫方 .钛合金的断口定量分析及环境敏感性[D].北京航空材料研究院博士后研究报告,2001. |
[19] | 谢明立;习年生;陶春虎 .疲劳应力的断口反推研究[J].航空材料学报,2001,21(01):32. |
[20] | 陶春虎,习年生,张卫方,谢明立.断口反推疲劳应力的新进展[J].航空材料学报,2000(03):158-163. |
[21] | 张卫方;高威;赵爱国.钛合金断口反推疲劳应力的实验与工程应用研究[J].机械强度 |
[22] | 张卫方,陶春虎,习年生,高威,刘高远.断口反推疲劳应力及其在叶片断裂分析中的应用[J].材料工程,2003(01):38-41. |
[23] | 李海燕,张学仁,阎晓军,聂景旭,陶春虎.旋转状态下叶片振动应力的断口反推法[J].航空学报,2001(04):303-307. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%