对热模压成型的聚酰亚胺(PI)试样在MHK-500型环-块摩擦试验机上测试了不同载荷P(N)、摩擦速度V(m·s-1)情况下,摩擦系数μ与摩擦持续时间t(min)的关系,并探讨了μ值随t,P,V变化的摩擦规律.结果表明V值增加,使第一阶段的μ峰值降低,峰值到来时间加快,峰宽变窄,第二阶段到来时间提前.而P值增加除了使μ峰值降低外,对第一、二阶段的其他参数的影响却相反.摩擦系数μ的表征值分别与P,V没有单值关系,而与单位面积所受的载荷P(MPa)和速度V的乘积pV值(MPa·m·s-1)具有指数关系.
参考文献
| [1] | FUSARO ROBERT L .Evaluation of several polymer materials for use as solid lubricants in space[J].Tribology Transactions,1987,31(02):174-181. |
| [2] | Bijwe J;TEWARI U S .Friction and wear studies of bulk polyetherimide[J].Journal of Materials Science,1990,25(01):548-556. |
| [3] | Fusaro R L;HADY W F .Tribological properties of graphitefiber-reinforced, partially fluorinated polyimide composites[J].ASLE Transactions,1986,29(02):214-222. |
| [4] | Bijwe J;TEWARI U S .Friction and wear studies of polyetherimide composites[J].WEAR,1990,138(06):61-76. |
| [5] | 丛培红,李同生,刘旭军,张绪寿,薛群基,李家泽.温度对线性和交联聚酰亚胺摩擦磨损性能的影响[J].高分子学报,1998(05):0. |
| [6] | 郑林庆.摩擦学原理[M].北京:高等教育出版社,1994 |
| [7] | LI TONGSHENG;CONG PEIHONG;LIU XUJUN .Tribophysical and tribochemical effects of a thermoplastic polyimide[J].Journal of Materials Science,2000(10):2597-2601. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%