通过两次包套锻造工艺细化了高Nb-TiAl合金铸态近片层组织.研究发现,两次锻造后接近二次锻造表面基本上是由大量的直线型或者流线型片层组织和少量的再结晶组织组成,而除此以外的大部分区域都发生了较大程度的再结晶,并且晶粒均匀细小.在(α+γ)两相区长时间热处理二次锻后组织可以有效消除β相,获得的仍然是双态组织.
参考文献
| [1] | 李书江 .高铌TiAl合金微合金化及蠕变性能的研究[D].北京科技大学,2001. |
| [2] | HUANGSC .MicrostructuresandpropertytradeoffsinwroughtTiAl-basealloys[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,1992,23:375. |
| [3] | 彭超群,黄伯云,贺跃辉.TiAl基合金的工艺-显微组织-力学性能关系[J].中国有色金属学报,2001(04):527-540. |
| [4] | SemiatinSL;SEETHARAMAN V;JAIN V K .Microstructuredevelopmentduringconventionalandisothermalhotforgingofanear-gammatitaniumaluminide[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,1994,25(12):2753-2768. |
| [5] | KimYW .Orderedintermetallicalloys,partⅢ:gammatitaniumaluminides[J].Journal of The Minerals,Metals & Materials Society,1994,46(07):30-39. |
| [6] | SemiatinSL .Segregationandhomogenizationofanear-gammatitaniumaluminide[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,1992,23(01):149-161. |
| [7] | SemiatinSL;CHESNUTT J C;AUSTIN C;SEETHARAMAN V.Processing of intermetallic alloys[M].TMS,1997 |
| [8] | G. E. Fuchs .Supertransus processing of TiAl-based alloys[J].Metallurgical and Materials Transactions, A. Physical Metallurgy and Materials Science,1998(1):27-36. |
| [9] | 闫蕴琪,王文生,张振祺,洪权,罗国珍,周廉,Zhou Lian.一种高性能TiAl金属间化合物[J].金属热处理学报,2000(03):1-5. |
| [10] | ZhangWJ;CHEN G L;WANG Y D;SUN Z Q .CharacteristicsofheatresistancealloysTi45Al10NbandTi48Al8Nb[J].Scripta Metallurgica et Materialia,1993,28:1113-1118. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%