采用电弧熔炼和机械合金化,随后在750℃,58MPa下热压制备了晶粒尺寸差别较大的Cu40Ni40Cr20合金,用X射线衍射仪、扫描电镜等分析手段对比研究了显微组织结构.结果表明:电弧熔炼制备的晶粒尺寸较大的Cu40Ni40Cr20合金为二相,组织极其不均匀;采用机械合金化,通过控制热压条件制备的纳米晶Cu40Ni40Cr20合金仍为双相,但显微组织均匀,稳定.随着球磨时间的延长,由于晶粒细化和应变的结果,衍射峰偏移并有明显的宽化产生,Cu在Cr或Cr在Cu中的固溶度明显增加,当球磨60h后,合金已由双相变成亚稳态的单相.由于机械合金化的粉末处于非平衡态,其超固溶度溶质随热压和真空退火过程的进行会慢慢脱溶分解出来,合金已由单相变为两相,两相颗粒均成倍长大,但仍然保持纳米级尺度;机械合金化、热压和退火后样品中Cu,Ni和Cr的晶格均未发生崎变;讨论了晶粒细化对合金显微组织的影响.
参考文献
| [1] | enjaminJS .Dispersionstrengthenedsuperalloysbymechanicalalloying[J].Metallurgical and Materials Transactions,1970,1:2943-2950. |
| [2] | enjaminJS;VOLIN T E .Themechanismofmechanicalalloying[J].Metallurgical and Materials Transactions,1974,5:1929-1933. |
| [3] | MURPHYR;COURTNEY T H .SynthesisofCu-NbCnanocompositesbymechanicalalloying[J].Nano-Structured Materials,1994,4:365-370. |
| [4] | AES;SAJI S;HORI S .MechanicalalloyingofAl-20%Timixedpowders[J].Journal of the Japan Institute of Metals,1990,54:895-902. |
| [5] | ZDUJICEM;KOBAYASHI K F;SHINGU P H .Mechanical alloying of Al-3 % mol fraction Mo powders[J].Zeitschrift fur Metallkunde,1990,81:380-385. |
| [6] | Xu J.;Klasse T.;Averback RS.;Herr U. .FORMATION OF SUPERSATURATED SOLID SOLUTIONS IN THE IMMISCIBLE NI-AG SYSTEM BY MECHANICAL ALLOYING[J].Journal of Applied Physics,1996(8 Pt.1):3935-3945. |
| [7] | ECKTR.A non-consumable metals anode for production of aluminum with low-temperature fluoride melts[J].Light Metals,1994:15417. |
| [8] | NIUY;GESMUNDO F;VIANI F .The air oxidation of twophase Cu-Cr alloys at 700-900℃-[J].Oxidation of Metals,1997,48:357. |
| [9] | HAUGSRUDR;KOFSTAD P .OnthehightemperatureoxidationofCu-richCu-Nialloys[J].Oxidation of Metals,1998,50:189. |
| [10] | VILLARSP.Hand of ternary alloy phase diagrams[M].Ohio:ASM,1997:8734. |
| [11] | WilliamG.The handbook of binary phase diagrams[M].New York: The General Electric Company,1978:820. |
| [12] | WANGCL.Densification phenomenon of powders by hot pressing[A].Kyoto:The Japan Society of Powders and Metallurgy,2000:793. |
| [13] | MartinG .Phasestabilityunderirradition:ballisticeffects[J].Physical Review,1984,30:1424. |
| [14] | ELLONP;AVERBACK F S .Nonequilibrium roughening of interfaces in crystals and shear: application to ball milling[J].Physical Review Letters,1995,74:1819. |
| [15] | KochCC .Synthesis of nanostructured materials by mechanical milling: problems and opportunities[J].Nanocrystalline Materials,1997,9:13. |
| [16] | 付广艳,牛焱,吴维.不同方法制备的Cu-Cr合金的氧化行为[J].金属学报,2003(03):297-300. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%