研究了碳纤维增强高韧环氧树脂5288复合材料薄壁圆管件的轴向压溃行为和引发角尺寸之间的关系.对15°,45°,60°引发角的相同尺寸试件分别进行轴向压溃试验,记录了试验过程中的结构载荷力-位移曲线,对照各组不同引发角的管形件轴向压溃过程的峰值压溃载荷、最小压溃载荷后发现,当引发角为60°时,结构的峰值压溃载荷最高,最小压溃载荷最低.对试验件失效后组织进行微观分析后发现,对应于不同引发角,由于接触状态不同,圆管件发生了不同方式的压溃失效,导致了结构吸能力-位移曲线的变化.
参考文献
| [1] | SOTIRISKELLAS .Design, fabrication and testing of a crushable energy absorber for a passive earth entry vehicle[R].NASA/CR 2002 - 211425 |
| [2] | POONC .A review of crashworthiness of composite aircraft structures[R].Ottawa: National Aeronautical EstablishmentAeronautical Note NAE-AN-63 NRC No: 31276,1990,2:1-34. |
| [3] | HULLD .Energyabsorbingcompositestructures[J].Sci · Techn Rev University of Wales,1988,3:23-30. |
| [4] | MIL-STD-1920A AV American military standard,light fixed and rotary-wing aircraft crash resistance[S].,1988. |
| [5] | FARLEYGL.Energy absorption of composite material and structures[A].St Louis USA,1987:613-627. |
| [6] | SIGALASI et al.Triggermechanicalinenergy-absorbingclasscloth/epoxytubes[J].Composites Science and Technology,1992,40:265-287. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%