针对铝合金腐蚀平均速率与瞬时速率的差异,根据腐蚀过程中试样横截面的变化与欧姆电阻的对应关系,建立了新的腐蚀速率计算方法.将试样全浸和半浸在腐蚀溶液中,分别测定了7075铝合金电阻随时间的变化,并由腐蚀速率计算公式获得了对应的腐蚀速率与时间的关系.结果表明,全浸6h前铝合金腐蚀速率随时间线性减小,接下来经历一个平坦区,25h后腐蚀速率又稍微增加.推断全浸6h之前铝合金表面主要发生点蚀,接下来是晶间腐蚀,25h之后进入剥蚀的发展期.铝合金半浸于电解液中的腐蚀速率随时间的变化趋势与全浸于溶液中相似.
参考文献
| [1] | KETCHAMSJ .Localized corrosion - cause of metal failure Exfoliation Corrosion of Aluminum Alloys[R].ASTM STP 516,1972. |
| [2] | HAIDEMENOPOULOSGN .Hydrogenabsorptioninto2024-T3aluminumalloyduringexfoliationandalternateimmersiontesting[J].CORROSION,1998,54(01):73-78. |
| [3] | CONDEA .Electrochemicalmodelingofexfoliationcorrosionbehaviorof8089alloys[J].Electrochimica Acta,1997,43(08):849-860. |
| [4] | F. Bellenger;H. Mazille;H. Idrissi .Use of acoustic emission technique for the early detection of aluminum alloys exfoliation corrosion[J].NDT & E international: Independent nondestructive testing and evaluation,2002(6):385-392. |
| [5] | HaashiM .Quantitative measurements of the degree of exfoliation on aluminum alloys[J].Corrosion Science,1993,35(1-4):169-183. |
| [6] | Andrieu C.;Rameau JJ.;Alcouffe F.;Reboul M.;Dalard F. .Aluminium alloy corrosion detection by magnetic measurements[J].Journal of Materials Science,1998(12):3177-3181. |
| [7] | 郭宝兰.LC4铝合金板材在EXCO溶液中的腐蚀行为[J].材料保护,1995(06):5. |
| [8] | 李荻,郭宝兰,张玉梅.硬铝合金剥蚀速率测试方法的研究[J].航空学报,1995(03):304. |
| [9] | 朱立群,李卫平,张琦.模拟实际飞机腐蚀介质中高强铝合金材料腐蚀行为研究[J].航空学报,1997(01):31. |
| [10] | 何建平,高亚东,樊蔚勋.评估航空铝合金剥蚀性能新方法的研究[J].腐蚀科学与防护技术,2003(01):18-20,28. |
| [11] | 化学工业部化工机械研究院.腐蚀与防护手册-腐蚀理论、实验及监测[M].北京:化学工业出版社,1995 |
| [12] | LY12CZ和7075T7351铝合金在EXCO溶液中腐蚀动力学的统计研究[J].航空学报,1999(01):34. |
| [13] | 李劲风,张昭,曹发和,程英亮,张鉴清,曹楚南.LC4铝合金剥蚀及其电化学阻抗行为[J].中国有色金属学报,2002(06):1189-1193. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%