以聚硅氧烷为先驱体,采用先驱体转化法制备SiCf/Si-O-C复合材料.研究了吸收剂含量不同对复合材料的弯曲强度、密度、热膨胀系数的影响,同时测试了材料对雷达波的反射率,结果表明低频带区有良好的吸波性能.对材料微观结构进行了分析讨论,发现界面结构与致密度是SiCf/Si-O-C复合材料具有高性能的主要原因.
参考文献
| [1] | 徐永东,成来飞,张立同.三维碳化硅/碳化硅陶瓷基编织体复合材料[J].无机材料学报,2001(02):344-348. |
| [2] | RSCHOLZ;F DOS SANTOS MARQUES .Electricalconductivityofsiliconcarbidecompositeandfibers[J].Journal of Nuclears,2002,307-311:1098-1101. |
| [3] | SPRINGERGD;WINDISCH C F .StabilityofSiC/SiCcompositesinenvironmentscontainingO2andH2[J].Journal of Nuclear Materials,1996,233-237:1271-1274. |
| [4] | MAQing-song;CHEN Zhao-hui .Processingandcharacterizationofthree-dimensionalcarbonfiberreinforcedSi-O-Ccompositeviaprecursorpyrolysis[J].Materials Science and Engineering,2003,352:213-216. |
| [5] | 马青松,陈朝辉,郑文伟,胡海峰.聚硅氧烷/二乙烯基苯的交联与裂解[J].国防科技大学学报,2001(05):40-44. |
| [6] | S. Rangarajan .Processing, physical and thermal properties of BlackglasTM matrix composites reinforced with NextelTM fabric[J].Journal of Materials Science,1999(3):515-533. |
| [7] | Mucalo MR.;Brown IWM.;Milestone NB. .NMR AND X-RAY DIFFRACTION STUDIES OF AMORPHOUS AND CRYSTALLIZED PYROLYSIS RESIDUES FROM PRE-CERAMIC POLYMERS[J].Journal of Materials Science,1997(9):2433-2444. |
| [8] | NAKANOK;KAMIYA A;NISHINO Y et al.Fabricationandcharacterizationsiliconcarbidecompositeandsiliconnitridecomposite[J].Journal of the American Ceramic Society,1995,78(10):2811-2814. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%