采用铝基粉芯丝材和电弧喷涂技术制备了铝基涂层,并研究了涂层的显微组织和抗氧化、耐腐蚀等性能.铝基原始涂层主要物相有AlFe,AlFe3,Al2O3,AlFe0.25 Ni0.77和AlNi等;经过800℃×1h热处理之后涂层中生成了高铝含量的新相Al3Ni4,Al86Fe14,Al5FeNi,提高了涂层的硬度.铝基涂层的抗氧化、耐腐蚀性能明显地优于相应的铁基涂层;其中Al-Fe-Ni-B铝基涂层抗氧化性能优良,接近于45CT;Al-Ni-Cr铝基涂层的耐腐蚀性能可与45CT相媲美.
参考文献
[1] | H.Q.Ye .Recent developments in high temperature intermetallics research in China[J].Intermetallics,2000(5/6):503-509. |
[2] | Zhang Zhonghua;Sun Yangshan;Liu Guijun;Guo Jun .Ductility improvement of Fe_3Al-based alloy with surface coating[J].Scripta materialia,1996(9):1071-1075. |
[3] | LACKFORDJR;BUCKLEY R A;JONES H .Spraydepositionofironaluminide[J].Journal of Materials Science,1998,33(09):4417-4421. |
[4] | GROSDIDIERTT;LIAO H L;TIDU A.X-rays and TEM characterization of nanocrystalline iron aluminide coatings prepared by HVOF thermal spraying[A].USA:Pub ASM International,2000 |
[5] | 朱子新,徐滨士,马世宁,杜则裕.高速电弧喷涂铁铝涂层的组织和性能[J].金属热处理,2002(03):12-13,28. |
[6] | 朱子新,徐滨士,张伟,杜则裕.高速电弧喷涂Fe-Al/WC复合涂层的组织和性能[J].材料工程,2002(05):18-21. |
[7] | UDIHARTONOSETIAMARGE .Devdopment of thermally sprayed Al-Cu-Fe-Cr quasicrystal coating[D].USA: University of Wisconsin-Madison,1997. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%