利用金相分析和扫描电镜对镍基高温合金电子束焊接热影响区微裂纹行为进行了分析.研究发现,熔合线附近的热影响区产生大量液化裂纹和沿晶扩展的固相裂纹.液化裂纹起源于MC碳化物的组份液化而形成的晶界连续或半连续的低熔点共晶液化膜,固相裂纹形成的则是高能电子束流的快速瞬态热冲击效应的直接结果.通过改善焊缝成形和提高焊接线能量有助于减小两类热影响区微裂纹倾向.
参考文献
| [1] | RICHARDSNL;NAKKALIL R;CHATURVEDI M C .Theinfluenceofelectron-beamweldingparametersonheat-affected-zonemicrofissuringinincoloy903[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,1994,25(08):1733-1744. |
| [2] | LUCASMJ;JACKSON C E .Theweldedheat-affectedzoneinnickelbasealloy718[J].Welding Journal,1970,49(02):46-54. |
| [3] | 张海泉 .电子束焊接瞬态热冲击效应研究[D].北京航空航天大学,2002. |
| [4] | 应慧筠;施成根;郝传勇 等.GH150合金电子束焊接热影响区液化与液化裂纹[J].金属学报,1997,33(09):995-1001. |
| [5] | Shinozakik;KUROKI H;LOU X J et al.ComparisonofhotcrackingsusceptibilitiesofvariousNi-base,heat-resistantsuperalloysbyU-typehotcrackingtest[J].Quarterly Journal of Japan Welding Society,1999,17(02):286-293. |
| [6] | 路文江;中尾嘉邦;莜崎贤二 .镍基合金焊接热影响区的液化裂纹[J].焊接学报,1993,14(03):186-194. |
| [7] | CHATURVEDIMC;RICHARDS NL;NAKKALI R et al.ElectronbeamweldingofaTi-45Al-2Nb-2Mn+08vol%TiB2XDalloy[J].Materials Science and Engineering A,1997,239-240:605-612. |
| [8] | 马翔生;毛智勇 .涡轮盘材料电子束焊接性分析[J].电子束加工技术,1999,1(z1):30-33. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%