Cu-Zn-Al合金经过简单的混合酸处理后,成功地在常温常压下制备出两种形态、组成不同的纳米管.能量衍射谱表明其主要成分是Cu,Zn,Al和Si,Al,O.其管径一般在20~50nm左右,最长长度达1600nm.研究发现,在混和酸处理后产生的分散程度很高的纳米粒子在纳米管的生长中起了重要作用,结合生长模型和透射电子显微镜照片初步分析了这种作用的机理和合金纳米管的生长机理.
参考文献
[1] | TENNE R;MARGULIS L;GENUT M et al.Polyhedral and cylindrical structures of WS2[J].Nature,1992,360:444-446. |
[2] | CHOPRA G C;LUYKEN R J;CHERREY K et al.Boron nitride nanotubes[J].Science,1995,296(18):966-967. |
[3] | Nath M.;Rao CNR.;Govindaraj A. .Simple synthesis of MoS2 and WS2 nanotubes[J].Advanced Materials,2001(4):283-286. |
[4] | Liao HW.;Zhang SY.;Qian YT.;Wang YF. .A solution low-temperature route to MoS2 fiber[J].Chemistry of Materials,2001(1):6-8. |
[5] | Jun Chen;Suo-Long Li;Qiang Xu;Koji Tanaka .Synthesis of open-ended MoS_2 nanotubes and the application as the catalyst of methanation[J].Chemical communications,2002(16):1722-1723. |
[6] | ROTHSCHILD A;POPPVITZ-BIRO R;LOURIE O et al.Morphology of multiwall WS2 nanotubes[J].Journal of Physical Chemistry B,2000,104:8976-8981. |
[7] | VOSSMEYER T;KATSIKAS L;GIERSIG M et al.CdS nanoclusters:synthesis,characterization,size dependent oscillator strength,temperature shift of the excitonic transition energy,and reversible absorbance shift[J].Journal of Physical Chemistry,1994,98:7665-7673. |
[8] | Zhu Y Q;HU W B;HOU W K et al.SiC-SiOX heterounction in nanowires[J].Journal of Materials Chemistry,1999,9(12):3173-3178. |
[9] | PAN Z W;DAI Z R;WANG Z L .Nanobelts of semiconducting oxides[J].Science,2001,291:1947-1949. |
[10] | GAO H X;LIU W H;LI B Y et al.Study of the non-liner oscillation pattern-self-organization phenomena on the surface of Cu-Zn-Al alloy[J].Journal of Tianjin University,1997,30:567-572. |
[11] | 黄惠忠.纳米材料分析[M].北京:化学工业出版社,2003:282-283. |
[12] | 高后秀;刘文华;李宝银 .Cu-Zn-Al合金表面非线性振荡花样[J].天津大学学报,1997,30(05):567-572. |
[13] | 杨新娥,高后秀,李京生,郑俊娟,杨渝钦.Cu-Zn-Al合金中类液振荡的非线性机理[J].物理学报,2001(07):1346-1349. |
[14] | 高后秀,张贵杰,麻亚宁,李桂杰,叶弘,杨渝钦.外加应力场刺激下固体"类流态"胞区的响应特征[J].材料热处理学报,2002(04):62-65. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%