对304奥氏体不锈钢进行固溶处理及随后的铁离子和氦离子辐照,并对三种处理试样进行超显微硬度测量和透射电镜下微观组织的观察.结果发现,相同的辐照能量和剂量下,两种离子辐照的硬化效果和微结构有较大的差异.铁离子辐照后试样的较浅层的硬化效果更显著,氦离子辐照后试样的较深层硬化效果更高些;铁离子辐照后试样表层辐照缺陷主要由高密度位错和位错缠结构成,氦离子辐照后表层辐照缺陷主要由细小致密的黑斑构成.
参考文献
| [1] | 杨武;张美杰;赵国珍 .304不锈钢在高温水中的应力腐蚀破裂[J].金属学报,1991,27B(02):116-120. |
| [2] | Yang W;ZHAO G;ZHANG M et al.An AES investigation of the surface films formed on stress corrosion test specimens of type 304 stainless steel in high temperature water[J].Corrosion Science,1992,33:89-102. |
| [3] | R. Nishimura;Sundjoro .Effects of chromate and molybdate on stress corrosion cracking of type 304 austenitic stainless steel in hydrochloric acid solution[J].Corrosion: The Journal of Science and Engineering,2000(4):361-370. |
| [4] | Kimoto T .Effects of composition and helium injection on dislocation loop development in pure Fe-Ni-Cr alloys under Ni ion irradiation[J].Journal of Nuclear Materials,1993,203:164-171. |
| [5] | Wang ZG.;Hou MD.;Jin GM.;Jin YF. .Modeling of damage creation in metallic materials under swift heavy ion irradiations[J].Nuclear Instruments and Methods in Physics Research, Section B. Beam Interactions with Materials and Atoms,2000(0):98-105. |
| [6] | X. L. Zhang;J. C. Jin .Stress corrosion studies of ion implanted austenitic steel[J].Journal of Materials Science,1999(9):2159-2162. |
| [7] | 田家万,韩增虎,赖倩茜,虞晓江,李戈扬.两步压入法--薄膜力学性能的可靠测量方法[J].机械工程学报,2003(06):71-74. |
| [8] | 万发荣.金属材料的辐射损伤[M].北京:科学出版社,1993 |
| [9] | 王广厚.粒子同固体相互作用物理学[M].北京:科学出版社,1991 |
| [10] | 胡传炘.表面处理技术手册[M].北京:北京工业大学出版社,2000 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%