讨论并分析了600℃的SiCp/ZA27熔体中超声的作用机理和有效作用范围.研究结果表明:在实验所用超声处理条件下(20kHz,1kW),ZA27合金熔体中声空化效应引发的熔体局部高压最大可达105MPa,局部高温可达1.77×104K;声流在熔体体系各个部位的作用强度不同,要获得优质的复合材料就必须在工艺上保证熔体的各个部位均能受到超声的有效作用.高能超声之所以能够制备出颗粒均匀分布、界面结合良好的SiCp/ZA27复合材料是高能超声在金属熔体中产生的声空化与声流共同作用的结果.
参考文献
| [1] | Yang Y;Lan J;Li XC .Study on bulk aluminum matrix nano-composite fabricated by ultrasonic dispersion of nano-sized SiC particles in molten aluminum alloy[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2004(1/2):378-383. |
| [2] | TSEUMEKAWA Y;SUZUKI H;OKUMIVA M .Preparation of in-situ reinforced composites using ultrasonic vibration and selective incorporation of reinforcements by magneticfield[J].Aluminum Transactions,2000,2(01):1-10. |
| [3] | XU ZH W;YAN J CH;WU G H et al.Interface structure of ultrasonic vibration aided interaction between Zn-Al alloy and Al2O3/6061Al composite[J].Journal of Materials Science Letters,1995,14(09):649-650. |
| [4] | 马立群;陈锋;舒光冀 .用高能超声法制备微细颗粒增强金属基复合材料[J].材料研究学报,1995,9(04):373-375. |
| [5] | Xia HS.;Wang Q. .Preparation of conductive polyaniline/nanosilica particle composites through ultrasonic irradiation[J].Journal of Applied Polymer Science,2003(11):1811-1817. |
| [6] | 何柞镛.声学理论基础[M].北京:国防工业出版社,1985 |
| [7] | 中西治通;恒川好树;毛利尚武 等.チタンアルナイド生成发热反应を应用レたアルミナ粒子/アルミニヱウム溶汤系の超声波溶浸[J].日本金属学会志(日本),1993,57:81-87. |
| [8] | AMBRAV O O V.Ultrasonic in liquid and solid metals[M].Boca Raton:CPC Press,1994 |
| [9] | 潘蕾 .高能超声作用下锌基复合材料的制备与研究[D].南京:东南大学,2004. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%