采用原位合成的方法制备了(Ti,V)C颗粒增强钢铁基复合材料,用XRD,SEM和电子探针研究了该复合材料的物相结构和显微组织,并用MM200型磨损试验机研究了该复合材料的耐磨性能.结果表明:原位合成的(Ti,V)C增强相颗粒细小,尺寸为1～2μm,呈球状,在α-Fe基体中均匀分布.在重载干摩擦磨损条件下,该复合材料显示了良好的耐磨性能.
参考文献
| [1] | WANG Yi-san;ZHANG Xin-yuan;LI Feng-chun .Study on an Fe-TiC surface composite produced in situ[J].Materials & Design,1999,20:233-236. |
| [2] | JONGMIN LEE;KWANGJUN EUH;JUN CHEOL OH .Microstructure and hardness improvement of TiC/stainless steel surface composites fabricated by high-energy electron beam irradiation[J].Materials Science and Engineering,2002,A233:201-259. |
| [3] | Y. C. Lin;S.W. Wang .Microstructure of TiC-W cladding on steel in nanoscale[J].Wear: an International Journal on the Science and Technology of Friction, Lubrication and Wear,2004(7/8):720-725. |
| [4] | Bourithis L.;Milonas A.;Papadimitriou GD. .Plasma transferred arc surface alloying of a construction steel to produce a metal matrix composite tool steel with TiC as reinforcing particles[J].Surface & Coatings Technology,2003(3):286-295. |
| [5] | Patrik Persson;Anders E. W. Jarfors;Steven Savage .Self-propagating high-temperature synthesis and liquid-phase sintering of TiC/Fe COMPOSITES[J].Journal of Materials Processing Technology,2002(2):131-139. |
| [6] | 王一三,张欣苑,黄文,李凤春.液态反应生成Fe-VC表面复合材料的组织与耐磨性能[J].复合材料学报,2000(01):71-75. |
| [7] | R. Sepulveda;F. Arenas .TiC-VC-Co: a study on its sintering and microstructure[J].International Journal of Refractory Metals & Hard Materials,2001(4/6):389-396. |
| [8] | 张卫方.SHS/PHIP技术制备TiC-30Fe金属陶瓷的显微组织及形成过程研究[J].材料工程,1998(10):15. |
| [9] | 熊惟皓;胡镇华;崔昆 .Ti(C,N)基金属陶瓷中包覆结构的研究[J].华中理工大学学报,1998,26(03):32-34. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%