在模拟油田CO2腐蚀环境下,进行Cr元素对P110钢耐腐蚀性能影响的实验.结果表明,Cr的加入没有改变温度对P110钢腐蚀特性的影响,两种钢的腐蚀速率都在90℃左右都达到最大值;温度对腐蚀具有双重作用,造成在温度小于90℃时表面形成的膜较疏松,保护性差,而温度大于90℃时,形成的膜和基体接触较为牢固,保护性强;钢中Cr元素的加入能有效地防止局部腐蚀的发生.
参考文献
| [1] | SCHMITT G.CO2 corrosion of steels-an attempt to range parameter and their effects[A].Houston:NACE,1984:1. |
| [2] | IKEDA A;VEDA M.CO2 corrosion behaviour of cr-containing steel,working arty eport on prediction CO2 corrosion in oil and gas Industry[A].Houston,NACE,1996:59-53. |
| [3] | 张学元;邸超;雷良才.二氧化碳腐蚀与控制[M].北京:化学工业出版社,2000 |
| [4] | MASAMURA K;INOHARA Y A;MINA MI Y U.Effects of C and N on corrosion resistance of high Cr alloys in CO2 and H2 S environments[A].Houston:NACE,1998:116. |
| [5] | CAYARD M S;KANE R D.Serviceability of 13Cr tubulars in oil and gas production environments[A].Houston:NACE,1998:112. |
| [6] | UEDA M;TAKABE H.Corrosion resistance of low Cr bearing steel in sour and sweet environments[A].Houston:NACE,2002:41. |
| [7] | NOSE K;ASAHI H;NICE P I;MARTIN J.Corrosion properties of 3%Cr steels in oil and gas environments[A].Houston:NACE,2001:82. |
| [8] | 陈长风,赵国仙,严密林,白真权,路民旭,杨延清.含Cr油套管钢CO2腐蚀产物膜特征[J].中国腐蚀与防护学报,2002(06):335-338. |
| [9] | BROOKS A R;CLAYTON C R;DOSS K;LU Y C .On the role of Cr in the passivity of stainless steel[J].Journal of the Electrochemical Society,1986,133(12):2459-2464. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%