利用溶胶-凝胶酸碱二步催化法和常压干燥法制备了SiO2干凝胶.反应物的配比是影响SiO2干凝胶制备最基本的因素.为了得到密度最小、孔隙率最大的SiO2干凝胶,本工作设计了一个四因素、三水平的正交实验确定水、无水乙醇、盐酸、氨水等反应物与正硅酸乙酯(TEOS)的摩尔比.同时为了保证所有实验均能在相同条件下发生,确定了其它实验参数.结果表明,SiO2干凝胶制备所需的最优反应摩尔配比为TEOS:水:无水乙醇:盐酸:氨水=1:4:10:7.5×10-4:0.0375.
参考文献
| [1] | 沈军;王珏;吴翔 .气凝胶-一种结构可控的新型功能材料[J].材料科学与工程,1994,12(03):1-5. |
| [2] | Hrubesh LW. .Aerogel applications[J].Journal of Non-Crystalline Solids: A Journal Devoted to Oxide, Halide, Chalcogenide and Metallic Glasses, Amorphous Semiconductors, Non-Crystalline Films, Glass-Ceramics and Glassy Composites,1998(1):335-342. |
| [3] | 栾军.现代试验设计优化方法[M].上海:上海交通大学出版社,1995 |
| [4] | Einarsrud MA.;Nilsen E.;Mortensen K.;Samseth J.;Kirkedelen MB. .Structural development of silica gels aged in TEOS[J].Journal of Non-Crystalline Solids: A Journal Devoted to Oxide, Halide, Chalcogenide and Metallic Glasses, Amorphous Semiconductors, Non-Crystalline Films, Glass-Ceramics and Glassy Composites,1998(1/2):10-16. |
| [5] | HAEREID S;NILSEN E;EINARSRUD M A .Properties of silica aged in TEOS[J].Journal of Non-Crystalline Solids,1996,204:228-234. |
| [6] | KISTLER S S .Coherent Expanded Aerogels and Jellies[J].Nature,1931,127:741. |
| [7] | Yu. K. Akimov .Fields of application of aerogels (review)[J].Instruments and Experimental Techniques,2003(3):287-299. |
| [8] | 李兴华.密度@浓度测量[M].北京:中国计量出版社,1991 |
| [9] | 沈军;王珏;吴翔 等.硅气凝胶的结构控制研究[J].材料科学与工艺,1994,4(02):87-93. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%