以TiCl4为主要原料,通过压力热晶法在300～400℃酸性条件下直接制备金红石型的TiO2纳米单晶,并通过TEM,XRD,HRTEM,FFT等技术手段对TiO2纳米晶的结构和形貌进行了表征.结果表明:高温和高压下有利于TiO2结晶成型.TEM显示:制备得到的TiO2纳米晶具有四方型结构外观,尺寸为十几到几百纳米,高温灼烧后纳米晶型不发生变化.XRD显示:制备得到的TiO2纳米晶是金红石型结构.
参考文献
| [1] | Yung-Fang Chen;Chi-Young Lee;Ming-Yu Yeng;Hsin-Tien Chiu .Preparing titanium oxide with various morphologies[J].Materials Chemistry and Physics,2003(1):39-44. |
| [2] | Li Y;White TJ;Lim SH .Low-temperature synthesis and microstructural control of titania nano-particles[J].International Journal of Quantum Chemistry,2004(4/5):1372-1381. |
| [3] | Eui Jung Kim;Sung-Hong Hahn .Microstructural changes of microemulsion-mediated TiO_2 particles during calcination[J].Materials Letters,2001(3/4):244-249. |
| [4] | Debao Wang;Caixia Song;Yusheng Lin .Preparation and characterization of TiO_2 hollow spheres[J].Materials Letters,2006(1):77-80. |
| [5] | 朱路平,宋海胜,廖桂红,贾志杰,黄在银.纳米氧化锡枝蔓晶的制备及形成机理[J].华中师范大学学报（自然科学版）,2005(02):228-231. |
| [6] | 张青红,高濂,郭景坤.四氯化钛水解法制备纳米氧化钛超细粉体[J].无机材料学报,2000(01):21-25. |
| [7] | 钱红梅,吴杰颖,李燕,郝成伟.液相法制备纳米TiO2[J].皖西学院学报,2005(02):42-44. |
| [8] | 刘威,陈爱平,林嘉平,戴智明,邱炜,刘伟,朱孟钦,臼田昭司.均相水解法制备金红石含量可控的纳米TiO2[J].化学学报,2004(12):1148-1152. |
| [9] | 张青红,高濂,郭景坤.四氯化钛水解法制备二氧化钛纳米晶的影响因素[J].无机材料学报,2000(06):992-998. |
| [10] | 徐惠,王毅,苟国俊,翟钧,曲晓丽,史建新.纳米TiO2的制备表征及其光催化性能研究[J].兰州理工大学学报,2005(04):68-71. |
| [11] | 徐建春,储伟,王安,邱发礼.受控水解法制备纳米TiO2光催化剂及其结构性能[J].化学研究与应用,2005(03):389-391. |
| [12] | Lei Miao;Sakae Tanemura;Shoichi Toh;Kenji Kaneko;Masaki Tanemura .Fabrication, characterization and Raman study of anatase-TiO_2 nanorods by a heating-sol-gel template process[J].Journal of Crystal Growth,2004(1/3):246-252. |
| [13] | 国伟林,王西奎,宋广智.超声化学法制备纳米二氧化钛[J].中国粉体技术,2002(04):22-23. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%