以钛酸丁酯为前驱体,采用溶胶-凝胶工艺制备了TiO2溶胶,并用浸渍提拉法在陶瓷基体上负载了TiO2薄膜.探讨了前躯体浓度和热处理方式对TiO2薄膜性能的影响.此外,通过XRD表征,检测了TiO2的晶体结构.结果表明:500℃下煅烧的TiO2薄膜为锐钛型结构;随着前驱体浓度的增大,薄膜的亲水性能变化不大,光降解性能逐渐提高;陶瓷片每负载一层TiO2薄膜后煅烧一次,薄膜的附着力提高.
参考文献
| [1] | KIM S;HONG S .Kinetic study of photocatalytic degradation of volatile organic compound in air using thin film TiO2 photocatalyst[J].Applied Catalysis B:Environmental,2002,15:305-315. |
| [2] | Piscopo A.;Marzolin C.;Weber JV.;Robert D. .TiO2 supported on glass fiber for the photocatalytic degradation of benzamide[J].Journal of Materials Science Letters,2000(8):683-684. |
| [3] | 杨术明,李富友,黄春辉.染料敏化纳米晶太阳能电池[J].化学通报,2002(05):292-296. |
| [4] | 张彭义,余刚,蒋展鹏.固定化二氧化钛膜的制备及其光催化性能[J].中国环境科学,2000(05):436-440. |
| [5] | 贺飞,唐怀军,赵文宽,方佑龄.二氧化钛光催化自洁功能陶瓷的研制[J].武汉大学学报(理学版),2001(04):419-424. |
| [6] | T. Watanabe;A. Nakajima;R. Wang;M. Minabe;S. Moizumi;A. Fujishima;K. Hashimoto .Photocatalytic activity and photoinduced hydrophilicity of titanium dioxide coated glass[J].Thin Solid Films: An International Journal on the Science and Technology of Thin and Thick Films,1999(12):260-263. |
| [7] | 张立德;牟季美.纳米材料科学[M].沈阳:辽宁科学技术出版社,1995 |
| [8] | 沈杰,董昊,张永熙.溶胶-凝胶法制备二氧化钛薄膜的亲水性研究[J].真空科学与技术学报,2000(06):385. |
| [9] | 唐振方,刘彭义,叶勤,孙汪典,余伟华.TiO2透明薄膜的制备与光诱导超亲水性研究[J].暨南大学学报(自然科学与医学版),2003(01):12-15. |
| [10] | Chen DW.;Ray AK. .Photodegradation kinetics of 4-nitrophenol in TiO2 suspension[J].Water research: A journal of the international water association,1998(11):3223-3234. |
| [11] | 王怡中,符雁,汤鸿霄.平板构型太阳光催化反应系统中甲基橙降解脱色研究[J].环境科学学报,1999(02):142-146. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%