利用等离子辉光放电溅射技术,在碳钢表面复合渗镀形成TiN扩散层和沉积层.表面成分检测渗镀层呈梯度材料分布,表面钛原子和氮原子之比,符合TiN相结构.渗镀层总深度约有15μm,表层TiN约有4μm.渗镀层成分检测表明,与基体之间呈梯度分布.X射线衍射结果表明,渗镀层表面为TiN,其中(200)晶面的衍射峰最强,具有明显的择优取向.TiN复合层在H2S溶液中的腐蚀行为表明:辉光合成的TiN涂层可以提高材料在富液溶液中的耐蚀性能,与PVD沉积TiN试样和基体低碳钢试样相比耐蚀性分别提高了5.76,49.76倍.
参考文献
| [1] | BEVERSKOG B;CARLSSON J O;DELBLANC BAUER A et al.Corrosion properties of TiC film prepared by active reactive evaporation[J].Surface and Coatings Technology,1990,41:221-225. |
| [2] | RUDENJA S;PAN J;LEYGRAF C et al.Passivation and anodic oxidation of duplex TiN coating on stainless steel[J].Journal of the Electrochemical Society,1999,146:4082-4087. |
| [3] | Marco J.F.;Gancedo J.R.;Hanzel D.;Agudelo A.C. .Corrosion resistance of single TiN layers, Ti/TiN bilayers and Ti/TiN/Ti/TiN multilayers on iron under a salt fog spray (Prohesion) test: An evaluation by XPS[J].Surface and Interface Analysis: SIA: An International Journal Devoted to the Development and Application of Techniques for the Analysis of Surfaces, Interfaces and Thin Films,1999(2):71-75. |
| [4] | CHEN B F;PAN W L;YU G P et al.On the corrosion behavior of TiN-coated AISI D2 steel[J].Surface and Coatings Technology,1999,111:16-20. |
| [5] | 高原.空心阴极辉光放电膏剂离子渗铝[J].中国腐蚀与防护学报,1997(03):23-25. |
| [6] | 李瑛,屈力,王福会,邵忠宝.TiN涂层电化学腐蚀行为研究Ⅰ.TiN涂层的保护性能与失效机制[J].中国腐蚀与防护学报,2003(02):65-69. |
| [7] | 周伟舫.电化学测量[M].上海:上海科学技术出版社,1985:290-296. |
| [8] | 刘烈炜 .在低pH值条件下微量H2S对碳钢腐蚀和渗氢过程的影响[J].石油与天然气化工,1999,28:23-25. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%