采用化学镀方法制备Ni-Co-P三元合金镀层以改善NdFeB磁体的耐腐蚀性能.优化了镀液配方以及施镀工艺,研究了镀液pH值和金属离子配比([Co2+]/[Ni2++Co2+])对沉积速度和镀层成分的影响,测量了NdFeB基体和不同镀层在3.5%(质量分数,下同)NaCl溶液中的极化曲线.结果表明,随镀液pH值增加,沉积速度提高,镀层中Co含量升高,Ni含量和P含量逐渐降低;随镀液中Co2+比例增加,沉积速度下降,镀层中Co含量升高,Ni和P含量降低.化学镀Ni-Co-P合金后的NdFeB磁体在3.5%NaCl溶液中的腐蚀速度降低了约两个数量级;当镀液金属离子配比[Co2+]/[Ni2++Co2+]=0.3时,镀层耐腐蚀性能最好,且优于相同施镀条件下所得到的Ni-P镀层.
参考文献
| [1] | El-Aziz AM.;Gutfleisch O.;Gebert A.;Schultz L.;Kirchner A. .Investigations of the corrosion behaviour of nanocrystalline Nd-Fe-B hot pressed magnets[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,2000(2):299-304. |
| [2] | ASSIS O B G;SINKA V;FERRANTE M et al.Electrochemical aspects of corrsion in sintered and hot-deformed Nd-Fe-B magnets[J].Journal of Alloys and Compounds,1995,218:263-266. |
| [3] | Turek K.;Liszkowski P. .The kinetics of oxidation of Nd-Fe-B powders[J].IEEE Transactions on Magnetics,1993(6):2782-2784. |
| [4] | Waldemar Kaszuwara;Marcin Leonowicz .Long-term corrosion tests on Nd-Fe-B sintered magnets[J].Materials Letters,1999(1):18-22. |
| [5] | Liszkowski P.;Figiel H.;Gajerski R.;Turek K. .The intermediate stages of the corrosion of Nd-Fe-B powders in ambient air[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,2001(1/2):270-275. |
| [6] | Cygan DF.;Mcnallan MJ. .CORROSION OF NDFEB PERMANENT MAGNETS IN HUMID ENVIRONMENTS AT TEMPERATURES UP TO 150-DEGREES-C[J].Journal of Magnetism and Magnetic Materials,1995(1/2):131-138. |
| [7] | Kim AS.;Lizzi T.;Camp FE. .HYDROGEN INDUCED CORROSION MECHANISM IN NDFEB MAGNETS[J].Journal of Applied Physics,1996(8 Pt.2a):4840-4842. |
| [8] | HU Y;AINDOW M;JONES L P et al.Effects of Zn deposit on the microstructure and magnetic properties of NdFeB magnets[J].Journal of Alloys and Compounds,2003,351:299-303. |
| [9] | Walton A.;Speight J.D. .A zinc coating method for Nd-Fe-B magnets[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,2000(1/2):253-261. |
| [10] | Blackwood DJ.;Huang YZ.;Tan CK.;Balakrisnan B. .Influence of the chemical composition of the plating solution on the ability of nickel coatings to protect Nd2Fe14B magnets against corrosion[J].Journal of Magnetism and Magnetic Materials,2001(2):103-111. |
| [11] | 李军,刘颖,高升吉,涂铭旌.粘结钕铁硼磁体阴极电泳工艺研究[J].腐蚀科学与防护技术,2005(02):121-124. |
| [12] | 郑华均,郑国渠,马淳安.化学镀镍磷合金工艺研究及其在钕铁硼永磁体抗蚀上的应用[J].表面技术,2002(02):42-45. |
| [13] | Kim DH.;Takano O.;Aoki K. .SOFT MAGNETIC FILMS BY ELECTROLESS NI-CO-P PLATING[J].Journal of the Electrochemical Society,1995(11):3763-3767. |
| [14] | Dong Nyung Lee;Kang-Heon Hur .THE EVOLUTION OF TEXTURE DURING ANNEALING OF ELECTROLESS Ni-Co-P DEPOSITS[J].Scripta materialia,1999(12):1333-1339. |
| [15] | I.H.M. Aly;M.M. Younan;M.T. Nageeb .Autocatalytic (Electroless) Deposition of Ternary Nickel-Cobalt-Phosphorus Alloy[J].Metal finishing,2003(4):37-42. |
| [16] | Younan MM.;Aly IHM.;Nageeb MT. .Effect of heat treatment on electroless ternary nickel-cobalt-phosphorus alloy[J].Journal of Applied Electrochemistry,2002(4):439-446. |
| [17] | 姜晓霞;沈伟.化学镀理论及实践[M].北京:国防工业出版社,2000 |
| [18] | 曹楚南.腐蚀电化学原理[M].北京:化学工业出版社,2004 |
| [19] | Narayanan TSNS.;Selvakumar S.;Stephen A. .Electroless Ni-Co-P ternary alloy deposits: preparation and characteristics[J].Surface & Coatings Technology,2003(2/3):298-307. |
| [20] | MATSUBARA H;YAMADA A .Control of magnetic properties of chemically deposited cobalt nickel phosphorus films by electrolysis[J].Journal of the Electrochemical Society,1994,141(09):2386-2390. |
| [21] | 赵麦群;雷阿丽.金属的腐蚀与防护[M].北京:国防工业出版社,2002 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%