在国内率先完成了新型八元系高强韧钛合金TC21的热模拟压缩变形实验,研究了TC21合金在β相区、(α+β)相区及相变点Tβ共8个温度点及0.01～50s-1等5个应变速率值条件下的单向热加工变形特性,重点对加工态金相组织、尤其是0.01s-1和50s-1条件下的组织进行了研究,结果发现,在试样的不同部位存在变形组织的不均匀现象,该合金在不同温度区域变形时分别发生重结晶和动态再结晶.重结晶导致晶粒粗化(约100～200μm),而动态再结晶致使晶粒细化(最小在1～2μm以下).
参考文献
| [1] | 赵永庆,曲恒磊,冯亮,杨海瑛,李辉,张颖楠,郭红超,黄定坤.高强高韧损伤容限型钛合金TC21研制[J].钛工业进展,2004(01):22-24. |
| [2] | 曲恒磊;赵永庆;朱知寿 等.一种高强韧钛合金及其加工方法[P].CN 03105965.1,2003-09-30. |
| [3] | Semiatin SL;Weiss I;Seetharaman V .Flow behavior and globularization kinetics during hot working of Ti-6Al-4V with a colony alpha microstructure[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,1999(2):257-271. |
| [4] | LI L X;LOU Y;YANG L B et al.Flow stress behavior and deformation characteristics of Ti-3Al-5V-5Mo compressied at elevated temperatures[J].Materials & Design,2002,23:451-457. |
| [5] | Weiss, I;Semiatin, SL .Thermomechanical processing of alpha titanium alloys--an overview[J].Materials Science & Engineering. A, Structural Materials: Properties, Microstructure and Processing,1999(2):243-256. |
| [6] | 曾卫东.Ti-17合金高温变形机理研究[J].材料工程,1996(09):27. |
| [7] | 赵永庆;周廉;邓炬.Ti-40阻燃钛合金的高温变形及本构方程建立机制[A].北京,1999:173-177. |
| [8] | 洪权,张振祺,赵永庆,曲恒磊,魏寿庸.Ti-6Al-2ZR-1Mo-1V合金的热压变形特性及塑性b动方程[J].广东有色金属学报,2001(02):129-133. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%