研究了化学复合镀镍-磷-金刚石镀层操作条件对复合镀层镀速、复合量及硬度的影响,并对复合镀层的组织和性能进行了分析.结果表明,金刚石颗粒在镀液中部分会被活化,进入复合镀层过程中其表面沉积有镍层.实验得到了镀速20μm/h以上、均匀的Ni-P-金刚石镀层,金刚石的加入对镀速的影响不大.金刚石在镀层中的质量分数主要与金刚石在溶液中含量有关,当金刚石在溶液中含量为20g/L时,其在镀层中质量分数可达15%,硬度可达HV(0.5)500以上,为Ni-P化学镀层硬度的2.5倍左右,且镀层硬度随镀层中金刚石含量增加而增大.复合镀层的耐蚀倾向与Ni-P化学镀层大致相同.
参考文献
[1] | 李宁;屠振密.化学镀实用技术[M].北京:化学工业出版社,2004 |
[2] | GARCIA I;FRANSAER J;CELIS J P .Electrodeposition and sliding wear resistance of nickel composite coatings containing micron and submicron SiC particles[J].Surface and Coatings Technology,2001,148(2-3):171-178. |
[3] | XU Hui;YANG Zhi;LI Meng-Ke et al.Synthesis and properties of electroless Ni-P-ND composite coatings[J].Surface and Coatings Technology,2005,191:161-165. |
[4] | GARCIA I;CONDE A;LANGELAAN G et al.Improved corrosion resistance through microstructural modifications induced by codepositing SiC-particles with electrolytic nickel[J].Corrosion Science,2003,45(06):1173-1189. |
[5] | J. N. Balaraju;S. K. Seshadri .Synthesis and characterization of electroless nickel-high phosphorus coatings[J].Metal finishing,1999(7):8-10,12-13-0. |
[6] | PERIENE N;CESUNIENE A;TAICAS L .Codeposition of mixtures of dispersed particles with nickel-phosphorus electrodeposits[J].Plating and Surface Finishing,1994,81(10):68-71. |
[7] | 郭鹤桐;张三元.复合镀层[M].天津:天津大学出版社,1991 |
[8] | 郭忠诚,朱晓云,杨显万.电沉积多功能复合材料的研究现状与展望[J].云南冶金,2002(03):128-137,164. |
[9] | 吴向清 .铝合金基电沉积Ni-SiC复合镀技术的研究[D].西北工业大学,2002. |
[10] | Sun Kyu Kim;Hong Jae Yoo .Formation of bilayer Ni-SiC composite coatings by electrodeposition[J].Surface & Coatings Technology,1998(1/3):564-569. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%