采用热压法制备了B4C/TiC/Mo陶瓷复合材料,分析了烧结工艺和TiC含量对B4C/TiC/Mo陶瓷复合材料力学性能和显微结构的影响.当烧结参数为1900℃,45min,35MPa时,85.3%(质量分数,下同)B4C/10%TiC/4.7%Mo陶瓷复合材料的抗弯强度、韧性、硬度和相对密度分别为705MPa,3.82MPa·m1/2,20.6GPa,98.2%.添加的TiC在烧结过程中与B4C发生化学反应生成了TiB2,利用生成的TiB2与添加的Mo协同增韧补强B4C/TiC/Mo陶瓷复合材料.
参考文献
| [1] | FRANCOIS THEVENOT .Boron carbide-a comprehensive review[J].Journal of the European Ceramic Society,1990,6(04):205-225. |
| [2] | DENG Jian-xin;ZHOU Jun;FENG Yi-hua et al.Microstructure and mechanical properties of hot-pressed B4C/(W,Ti)C ceramic composites[J].Ceramics International,2002,28:425-430. |
| [3] | ALIZADEH A;TAHERI-NASSAJ E;EHSANI N .Synthesis of boron carbide powder by a carbothermic reduction method[J].Journal of the European Ceramic Society,2004,24(10-11):3227-3234. |
| [4] | SIGL L S .Processing and mechanical properties of boron carbide sintered with TiC[J].Journal of the European Ceramic Society,1998,18:1521-1529. |
| [5] | Kustas F.;Zhou J.;Mishra B. .Wear behavior of B4C-Mo co-sputtered wear coatings[J].Surface & Coatings Technology,2001(1):48-54. |
| [6] | HUANG Qi-zhong;YANG Qiao-qin;DU Hai-qing et al.Effect of TiC on the microstructure and properties of C-B4C-SiC composite[J].CARBON,1995,2:9-13. |
| [7] | Zhen Yuhua;Li Aiju;Yin Yansheng;Shi Ruixia;Liu Yingcai .Reactive and dense sintering of reinforced-toughened B_4C matrixcomposites[J].Materials Research Bulletin: An International Journal Reporting Research on Crystal Growth and Materials Preparation and Characterization,2004(11):1615-1625. |
| [8] | SCHWETZ K A;GRELLNER W .The influence of carbon on the microstructure and mechanical properties of sintered boron carbide[J].Journal of the Less Common Metals,1981,82:37-47. |
| [9] | Schwetz KA.;Pfau L.;Sigl LS. .MECHANICAL PROPERTIES OF INJECTION MOLDED B4C-C CERAMICS[J].International Journal of Quantum Chemistry,1997(1):68-76. |
| [10] | KNUDSEN F P .Dependence of the mechanical properties of brittle polycrystalline specimens on porosity and grain size[J].Journal of The American Chemical Society,1959,42:376-387. |
| [11] | COBLE R L;KINGERY W D .Effect of porosity on physical properties of sintered alumina[J].Journal of The American Chemical Society,1956,39:377-385. |
| [12] | SUZUYA YAMADA;KIYOSHI HIRAO;YUKIHIKO YAMAUCHI et al.B4C-CrB2 composites with improved mechanical properties[J].Journal of the European Ceramic Society,2003,23:561-565. |
| [13] | 刘宁,胡镇华,崔昆.Mo在颗粒型复合材料金属陶瓷中的作用[J].稀有金属材料与工程,1994(03):45-48. |
| [14] | 许育东,刘宁,石敏,韩成良,晁晟.Mo添加量对纳米改性金属陶瓷显微组织的影响[J].矿冶工程,2005(02):77-80. |
| [15] | 孙德明,刘立红,鹿晓阳,许崇海,张勤河,艾兴.Al2O3/Cr3C2/（W,Ti）C陶瓷材料的力学性能及微观结构[J].硅酸盐学报,2005(04):411-415. |
| [16] | 唐国宏,陈昌麒,张兴华.B4C-TiB2-W2B5复合材料研究[J].航空学报,1994(06):761. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%