采用纳米碳酸钙、纳米铜粒子混合物作为润滑油添加剂.选择合适的表面活性剂制备含纳米碳酸钙和纳米铜粒子混合物添加剂的润滑油.利用四球摩擦磨损试验机考察含纳米碳酸钙、纳米铜粒子添加剂的润滑油的摩擦学性能;用扫描电子显微镜(SEM)观察表面磨痕的形貌.用原子力显微镜和扫描电子显微镜(SEM)观察分析在磨损表面纳米粒子的形态与分布.研究结果表明,纳米碳酸钙、纳米铜的粒子混合物的最佳添加量为:纳米碳酸钙与纳米铜的总添加量的质量分数为0.6%,纳米碳酸钙与纳米铜的质量分数之比为1∶1;该润滑油具有最佳的摩擦学性能.研究还表明,润滑油中纳米碳酸钙、纳米铜粒子混合物添加剂的优良摩擦学性能与纳米粒子在表面存在形态相关.
参考文献
| [1] | S. Tarasov;A. Kolubaev;S. Belyaev;M. Lerner;F. Tepper .Study of friction reduction by nanocopper additives to motor oil[J].Wear: an International Journal on the Science and Technology of Friction, Lubrication and Wear,2002(1/2):63-69. |
| [2] | RAPOPORT L;LVOVSKY M;LAPASKER I et al.Friction and wear of bronze power composites including fullerene-like WS2 nanoparticles[J].Wear,2001,249:150-157. |
| [3] | CHHOWALLA M;AMARATUNGA G A J .Thin film of fullerene-like MoS2 nanoparticles with ultra-low friction and wear[J].NATURE,2000,407:164-167. |
| [4] | CIZAIRE L;VACHER B;LE MOGNE T et al.Mechanism of ultra low friction by hollow inorganic fullerene-like MoS2 nanoparticles[J].Surface and Coatings Technology,2002,160:282-287. |
| [5] | 党鸿辛,赵彦保,张治军.铋纳米微粒添加剂的摩擦学性能研究[J].摩擦学学报,2004(02):185-187. |
| [6] | 沃恒洲,胡坤宏,胡献国.纳米二硫化钼作为机械油添加剂的摩擦学特性研究[J].摩擦学学报,2004(01):33-37. |
| [7] | 董国军,罗云霞,曲建俊.纳米金属粉在润滑中的应用[J].润滑与密封,2004(06):115-117,124. |
| [8] | 霍玉秋,闫玉涛,刘晓霞,丁津原,翟玉春,田彦文.单分散纳米SiO2的制备及其作为润滑油添加剂的摩擦学性能研究[J].摩擦学学报,2005(01):34-38. |
| [9] | 刘维民.纳米颗粒及其在润滑油脂中的应用[J].摩擦学学报,2003(04):265-267. |
| [10] | 岳美娥,周惠娣.纳米微粒在摩擦学中的应用研究[J].润滑与密封,2003(02):85-87. |
| [11] | GB/T 12583-1998.GB/T 12583-1998.润滑剂极压性能测定法(四球法)[S].,1998. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%