通过声电沉积在碳/碳复合材料表面制备钙磷生物活性涂层,采用SEM(带EDAX)或FE-SEM,XRD,FTIR研究电解质浓度和初始pH值对钙磷生物活性涂层的形貌、结构和组成的影响,并采用拉伸测试评价涂层与基体的结合力.结果表明:随着电解质浓度的降低,其组成由羟基磷灰石与磷酸三钙组成的混合涂层转变为含碳酸根的羟基磷灰石涂层,n(Ca)/n(P)和碳酸根的含量逐渐增加,片状晶体颗粒减小.随着初始电解液pH值的升高,涂层致密,均为片状含碳酸根的羟基磷灰石,n(Ca)/n(P)呈增加的趋势,片状晶体的厚度在30～40nm之间.涂层拉伸实验表明:小电解质浓度时,其涂层与基体的结合强度(5.62MPa)大于高电解质浓度时涂层与基体的结合强度(3.85MPa).
参考文献
| [1] | BRUCKMANN H;HUTTINGER KJ .Carbon,a promising material in endoprosthetics.Part 1:the carbon materials and their mechanical properties[J].Biomaterials,1980,1(02):67-72. |
| [2] | BRUCKMANN H;KEUSCHER G;HUTTINGER KJ .Carbon,a promising material in endoprosthetics.Part 2:tribological properties[J].Biomaterials,1980,1(02):73-81. |
| [3] | ADAMS D;WILLIAMS DF;HILL J .Carbon fiber-reinforced carbon as a potential implant material[J].Journal of Biomedical Materials Research,1978,12(01):35-42. |
| [4] | GWYN M JENKINS;FRANCISCO X;DE CARVALHO .Biomedical applications of carbon fiber reinforced carbon in implanted prostheses[J].CARBO,1977,15(01):33-37. |
| [5] | Yen SK.;Lin CM. .Cathodic reactions of electrolytic hydroxyapatite coating on pure titanium[J].Materials Chemistry and Physics,2003(1):70-76. |
| [6] | 俞耀庭;张兴栋.生物医用材料[M].天津:天津大学出版社,2000 |
| [7] | 翟言强,李克智,李贺军,刘皓,赵建国.碳/碳复合材料表面改性及其生物响应特性[J].材料工程,2006(04):60-66. |
| [8] | 隋金玲,李木森,吕宇鹏.人体承重骨替换用碳/碳复合材料的研究现状[J].生物医学工程学杂志,2004(04):686-689. |
| [9] | 张秀莲,熊信柏,黄剑锋,李贺军,黄敏,马威,王新木.炭/炭复合材料表面生物活性钙磷涂层XRD和Raman光谱研究[J].新型炭材料,2003(02):123-127. |
| [10] | 熊信柏,李贺军,李克智,黄剑锋,马威,王新木.电流密度对声电沉积生物活性透钙磷石涂层结构和形貌的影响[J].稀有金属材料与工程,2003(11):923-926. |
| [11] | 熊信柏,李贺军,黄剑锋,黄敏,孙国栋.声作用功率对炭/炭复合材料表面磷酸钙生物活性陶瓷涂层的影响[J].新型炭材料,2004(01):33-37. |
| [12] | 叶佩文.硅酸盐物理与化学[M].南京:东南大学出版社,1998 |
| [13] | Stigter M;de Groot K;Layrolle P .Incorporation of tobramycin into biomimetic hydroxyapatite coating on titanium.[J].Biomaterials,2002(20):4143-4153. |
| [14] | 熊信柏,李贺军,黄剑锋,李克智,白瑞成,孙国岭.碳/碳复合材料表面声电沉积/碱热处理复合工艺制备羟基磷灰石生物活性涂层研究[J].稀有金属材料与工程,2005(09):1489-1492. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%