研究了TA15钛合金片状和双态两种典型组织对疲劳性能和断裂韧度的影响,结果表明:在S-N曲线的高应力区,双态组织的疲劳强度高于片状组织;在低应力区,情况则相反,且片状组织的疲劳极限(656MPa)高于双态组织(565MPa).片状组织的疲劳裂纹扩展速率低于双态组织,且断裂韧度K1C高于双态组织,即片状组织的损伤容限性能优于双态组织.
参考文献
| [1] | 曹春晓.选材判据的变化与高损伤容限钛合金的发展[J].金属学报,2002(z1):4-11. |
| [2] | R. Filip;K. Kubiak;W. Ziaja;J. Sieniawski .The effect of microstructure on the mechanical properties of two-phase titanium alloys[J].Journal of Materials Processing Technology,2003(1/2):84-89. |
| [3] | LüTJERING G .Influence of processing on microstructure and mechanical properties of α+β titanium alloys[J].Materials Science and Engineering A:Structural Materials Properties Microstructure and Processing,1998,A243:32-45. |
| [4] | WANHILL R J H .Ambient temperature crack growth in titanium alloys and its significance for aircraft structures[J].Aeronautical Journal,1977,81:68-82. |
| [5] | CRICHLOW W J.High cycle fatigue properties of titanium in aircraft application[A].New York-London:Plenum Press,1973:1257-1270. |
| [6] | HINES J A;TJERING G .Propagation of microcracks at stress amplitudes below the conventional fatigue limit in Ti-6A1-4V[J].Fatigue Fract Engng Mater Structure,1999,22:657-665. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%