利用AC-HAVF喷涂技术在0Cr13Ni5Mo不锈钢上制备了WC-10Co-4Cr,WC-12Co涂层,并利用XRD,SEM,电化学以及盐雾实验分析了涂层的微观组织以及耐蚀性.结果表明:两种涂层相组成与其粉末一致,未出现其他喷涂技术普遍存在的W2C以及W,AC-HAVF喷涂技术可以有效的抑制WC的分解;两种涂层都很致密且与基体结合良好,孔隙率低;电化学以及盐雾实验发现,WC-10Co-4Cr涂层的耐蚀性好于WC-12Co涂层,并较基体0Cr13Ni5Mo不锈钢有较大的提高,粘结相中Cr元素的加入以及孔隙率低是WC-10Co-4Cr涂层耐蚀性优异的重要原因.
参考文献
[1] | 樊自拴,孙冬柏,俞宏英,李辉勤,孟惠民,张济山,乔力杰.超音速火焰喷涂技术研究进展[J].材料保护,2004(09):33-35. |
[2] | JIN H W;KIM M C;PARK C G.Friction-induced solid state amorphization from non-equilibrium solid solution phase in Fe-Cr-B-Ni-Mo spray coatings[A].,2003:279-286. |
[3] | ZIMMERMAN S;KELLER H;SCHWIER G.New carbide based materials for spraying[A].Ohio,USA:Asm international,Materials Park,2003:227-233. |
[4] | V. Stoica;R. Ahmed;T. Itsukaichi;S. Tobe .Sliding wear evaluation of hot isostatically pressed (HIPed) thermal spray cermet coatings[J].Wear: an International Journal on the Science and Technology of Friction, Lubrication and Wear,2004(11):1103-1124. |
[5] | Qiao YF.;Fischer TE.;Dent A. .The effects of fuel chemistry and feedstock powder structure on the mechanical and tribological properties of HVOF thermal-sprayed WC-Co coatings with very fine structures[J].Surface & Coatings Technology,2003(1):24-41. |
[6] | T. Sudaprasert;R. H. Shipway;D. G. McCartney .Sliding wear behaviour of HVOF sprayed WC-Co coatings deposited with both gas-fuelled and liquid-fuelled systems[J].Wear: an International Journal on the Science and Technology of Friction, Lubrication and Wear,2003(7/12):943-949. |
[7] | Li H;Khor KA;Yu LG;Cheang P .Microstructure modifications and phase transformation in plasma-sprayed WC-Co coatings following post-spray spark plasma sintering[J].Surface & Coatings Technology,2005(1):96-102. |
[8] | H. Liao;B. Normand;C. Coddet .Influence of coating microstructure on the abrasive wear resistance of WC/Co cermet coatings[J].Surface & Coatings Technology,2000(2/3):235-242. |
[9] | Cho JE;Hwang SY;Kim KY .Corrosion behavior of thermal sprayed WC cermet coatings having various metallic binders in strong acidic environment[J].Surface & Coatings Technology,2006(8):2653-2662. |
[10] | Souza VAD.;Neville A. .Linking electrochemical corrosion behaviour and corrosion mechanisms of thermal spray cermet coatings (WC-CrNi and WC/CrC-CoCr)[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2003(1/2):202-211. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%