通过蠕变曲线的测定及组织形貌的观察,研究了FGH95粉末镍基合金的蠕变行为及变形特征.结果表明:FGH95粉末镍基合金在试验的温度和应力范围内,具有明显的施加温度和应力敏感性,并测算出合金的蠕变激活能和应力指数.合金的组织结构由一次、二次、三次γ'相及弥散分布的碳化物组成,在粉末颗粒之间具有较宽的晶界.蠕变期间,在合金晶粒内的变形以单取向或双取向滑移方式进行,并在滑移迹线附近有细小碳化物析出,而较宽的晶界由于剧烈变形可发生碎化形成细小晶粒.合金在蠕变期间的微观变形机制是位错发生双取向滑移,其中(1/2)《110》位错在γ基体相中运动,《110》超位错存在于γ'相内,而层错的形成是由于《110》超位错分解为(1/3)《112》超肖克莱不全位错所致.
参考文献
| [1] | 张义文,杨士仲,李力,李世魁,张莹,张凤戈,国为民,冯涤.我国粉末高温合金的研究现状[J].材料导报,2002(05):1-4. |
| [2] | 江和甫.对涡轮盘材料的需求及展望[J].燃气涡轮试验与研究,2002(04):1-6. |
| [3] | 陈焕铭,胡本芙,李慧英,宋铎.等离子旋转电极雾化FGH95高温合金粉末的预热处理[J].中国有色金属学报,2003(03):554-559. |
| [4] | 张义文 .俄罗斯粉末冶金高温合金[J].钢铁研究学报,1998,10(03):74-76. |
| [5] | Lherbier L W;Kent W B .Technical and economic aspects of powder metallurgy superalloys[J].International Journal of Powder Metallurgy,1990,26(02):131-137. |
| [6] | Ramakrishnan R I;Howson T E.Modeling the heat treatment of superalloys[J].Journal of Materials Science,1992(06):29-32. |
| [7] | Park N K;Kim I S .Hot forging of nickel-base superalloy[J].Journal of Materials Processing Technology,2001,111(02):98-102. |
| [8] | Youdelis W V;Kwon O .Carbide phases in nickel based superalloy nucleation properties of MC type carbide[J].Metal Science Journal,1983,17(08):385-388. |
| [9] | HU Ben-fu;HE Cheng-qun;GAO Qing et al.The formation mechanism of partial recrystallization zone and quenching crack in FGH95 alloy[J].Acta Matallurgica Sinica,1999,35(02):363-367. |
| [10] | 陈焕铭,胡本芙,余泉茂,宋铎.FGH95粉末枝晶间合金元素偏析的研究[J].材料工程,2002(03):32-35. |
| [11] | 国为民,张凤戈,张莹,张义文.镍基粉末高温合金的组织、性能与成型和热处理工艺关系的研究[J].材料导报,2003(03):11-15. |
| [12] | Shamblen C E;Chang D R .Effect of inductions on LCF life of HIP plus treatment powder metal Rene95[J].Metallurgical and Materials Transactions,1985,16:775-784. |
| [13] | Klepser C A .Effect of continuous cooling rate on the precipitation of gamma prime in nickel-based superalloys[J].Scripta Metallurgical,1995,33(04):589-596. |
| [14] | TIAN Su-gui;Yu Xing-fu;YANG Jing-hong et al.Deformation features of a nickel-base superalloy single crystal during compress creep[J].Materials Science and Engineering A,2004,379:141-147. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%