用粉末-溶胶混合物挤出法制备了直径为300μm和400μm的PZT压电纤维,研究了纤维的显微结构、密度和收缩率.采用排列-浇铸法制备了纤维体积分数为25%的1-3型压电纤维复合材料,计算了材料的介电常数、机电耦合系数和机械品质因数.结果表明:1-3型压电复合材料的Kp小于压电陶瓷片,Kt和Kt/Kp都大于陶瓷片;相同体积分数的压电纤维复合材料,直径为400μm的纤维制备的复合材料其εT,d33,Kt和Kt/Kp都大于直径为300μm的纤维制备的复合材料.
参考文献
| [1] | R.Brett Williams;Daniel J.Inman;Marc R.Schultz;Michael W.Hyer;W.Keats Wilkie .Nonlinear Tensile and Shear Behavior of Macro Fiber Composite Actuators[J].Journal of Composite Materials,2004(10):855-869. |
| [2] | Wickramasinghe VK;Hagood NW .Material characterization of active fiber composites for integral twist-actuated rotor blade application[J].Smart Materials & Structures,2004(5):1155-1165. |
| [3] | 党长久;李明轩 .1-3型压电复合材料[J].应用声学,1995,14(01):2-7. |
| [4] | Klicker K A;Bigger J V;Newnham R E et al.Composites of pzt and epoxy for hydrostatic transducer applications[J].Journal of the American Ceramic Society,1981,64(01):5-9. |
| [5] | Klicker K A;Newnham R E;Cross L E et al.PZT composite and a fabrication method thereof[P].US 4412148,1983. |
| [6] | 张沛霖;张仲渊.压电测量[M].北京:国防工业出版社,1983:178-300. |
| [7] | 杨凤霞 .聚合物基压电复合材料的设计及机理研究[D].中国科学院武汉物理与数学研究所,2004. |
| [8] | 徐玲芳 .1-3型PZT5/epoxy resin压电复合材料的制备、结构与性能研究[D].武汉理工大学,2006. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%