采用固相合成法制备了Y2O3掺杂(Bi0.5 Na0.5)0.94 Ba0.06 TiO3无铅压电陶瓷.研究了Y2O3掺杂对(Bi0.5 Na0.5)0.94Ba0.06 TiO3陶瓷晶体结构、介电与压电性能的影响.XRD分析表明,在所研究的组成范围内陶瓷均能够形成纯钙钛矿固溶体.介电常数-温度曲线显示陶瓷具有弛豫铁电体特征,陶瓷的弛豫特征随掺杂的增加更为明显.在Y2O3掺杂量为0.5%时陶瓷的压电常数d33分别为137 pC/N,为所研究组成中的最大值,掺杂量为0.1%时,机电耦合系数kp与kt最大值为0.30,0.47.

参考文献

[1] TAKENAKA T;SAKATA K .Dielectric piezoelectric and pyro-eletric properties of Bi/2Na1/2TiO3-based ceramics[J].Ferroelectrics,1989,95(01):153-156.
[2] TAKENAKA T;MARUYAMA K;SAKATA K .Bi1/2 Na1/2 TiO3-BaTiO3 system for lead-free piezoelectric ceramics[J].Japanese Journal of Applied Physics,1991,30(9B):2236-2239.
[3] H. Nagata;N. Koizumi;T. Takenaka .Lead-Free Piezoelectric Ceramics of (Bi_1/2Na_1/2)TiO3-BiFeO3 System[J].Key engineering materials,1999(287):37-40.
[4] Hajime Nagata;Tadashi Takenaka .Additive effects on electrical properties of (Bi_(1/2)Na_(1/2))TiO_3 ferroelectric ceramics[J].Journal of the European Ceramic Society,2001(10/11):1299-1302.
[5] SASKI A;CHIBA T .Dielectric and Piezoelectric Properties of (Bi0.5 Na0.5) TiO3-(Bi0.5 K0.5) TiO3 System[J].Japanese Journal of Applied Physics,1999,38:5564-5567.
[6] TAKENAKA T;OKUDA T .Lead free piezoelectric ceramics based on Bi1/2 Na1/2 TiO3-NaNbO3[J].FERROELECTRICS,1997,196:175-178.
[7] SAKATA K;TAKENAKA T;NAITON Y .Phase relations,di-electric and piezoelectric properties of ceramics in the system (Bi0.5 Na0.5) TiO3-PbTiO3[J].Ferroelectrics,1992,131:219-222.
[8] LI H D;FENG C D;YAP W L .Some effects of different addi-tives on dielectric and piezoelectric properties of Bi1/2 Na1/2 TiO3-BaTiO3 morphotropic-phase-boundary composition[J].Materials Letters,2003,58(7-8):1194-1198.
[9] XU Qing;ZHAO Xing-zhong .Processing and properties of CeO2-doped ferroelectric (Bi0.5 Na0.5)0.04 Ba0.06 TiO3[J].Materials Letters,2006,60(07):11453-1458.
[10] SMOLENSKII G A;ISUPOV V A;AGRANOVSKAYA et al.Ferroelectrics with diffuse phase transition[J].Physics of the Solid State,1996,11(02):2584-2589.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%