通过超重力场制备了纳米碳酸钙,对纳米碳酸钙进行超声波分散,然后进行原位乳液聚合,采用分步聚合的方式,在纳米碳酸钙表面包覆了丙烯酸酯类共聚物,制得了纳米碳酸钙表面原位聚合包覆产物.采用TEM、DSC、TGA和表面电子能谱(ESCA)对纳米碳酸钙表面原位聚合包覆产物进行了表征.结果表明:制备的纳米碳酸钙粒子粒径在20nm左右,通过原位乳液聚合包覆后,粒径在40～80nm,包覆后的纳米碳酸钙复合粒子表面几乎不含Ca元素,表明纳米碳酸钙被良好包覆,并形成了以纳米碳酸钙为核、PBA为中间层、MMA和EA,St共聚物为壳的三层结构有机-无机纳米复合粒子.
参考文献
| [1] | Tom Hasell;Jixin Yang;Wenxin Wang .Preparation of polymer-nanoparticle composite beads by a nanoparticle-stabilised suspension polymerisation[J].Journal of Materials Chemistry: An Interdisciplinary Journal dealing with Synthesis, Structures, Properties and Applications of Materials, Particulary Those Associated with Advanced Technology,2007(41):4382-4386. |
| [2] | 张立德.纳米材料[M].北京:化学工业出版社,2000 |
| [3] | 张志昆;崔柞林.纳米技术与纳米材料[M].北京:国防工业出版社,2000 |
| [4] | Guo TY.;Tang GL.;Hao GJ.;Song MD.;Zhang BH. .Toughening modification of PS with n-BA/MMA/styrene core-shell structured copolymer from emulsifier-free emulsion polymerization[J].Journal of Applied Polymer Science,2003(5):1290-1297. |
| [5] | K. Mylvaganam;L. C. Zhang .A Cross-scale Characterization of Interface Properties between Carbon Nanotubes and Polymer Matrix[J].Key engineering materials,2006(312):217-222. |
| [6] | Wang GJ;Klang CS;Jin RG .Synthesis of acrylic core-shell composite polymers and properties of plastisol-gels[J].Progress in Organic Coatings: An International Review Journal,2004(1):55-61. |
| [7] | 权英,杨明山,严庆,王志勋,金日光.纳米刚性粒子对硬质PVC的增韧增强效果[J].北京化工大学学报(自然科学版),2002(06):23-26. |
| [8] | Quan Y;Yang MS;Liang TX;Yan Q;Liu DS;Jin RG .Effects of the reinforcement and toughening of acrylate resin/CaCO3 nanoparticles on rigid poly(vinyl chloride)[J].Journal of Applied Polymer Science,2007(6):3940-3949. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%