以KMnO4为氧化剂,以NaHSO2为阴离子还原剂制备了超级电容器用MnO2.运用N2吸附、SEM和XRD对氧化锰进行了形貌和结构表征.通过循环伏安和恒流充放电测试研究了氧化锰的电化学性能.结果表明:实验制备的MnO2为无定型结构,粒径为20~40nm,比表面积为155.4m2·g-1.在1mol·L-1的(NH4)2SO4溶液中,在-0.4~0.5V(vs SCE)的电位范围内表现出典型的法拉第赝电容行为,电流密度为10mA·cm-2时,其比容达到325 F·g-1.
参考文献
[1] | Nakayama M;Kanaya T;Inoue R .Anodic deposition of layered manganese oxide into a colloidal crystal template for electrochemical supercapacitor[J].Electrochemistry communications,2007(5):1154-1158. |
[2] | NGAGRARAJAN N;CHEONG M;ZHITOMIRSKY I .Electrochemical capacitance of MnO2 films[J].Materials Chemistry and Physics,2007,103:47-53. |
[3] | Lin CK;Chuang KH;Lin CY;Tsay CY;Chen CY .Manganese oxide films prepared by sol-gel process for supercapacitor application[J].Surface & Coatings Technology,2007(4/7):1272-1276. |
[4] | Li XL;Li WJ;Chen XY;Shi CW .Hydrothermal synthesis and characterization of orchid-like MnO2 nanostructures[J].Journal of Crystal Growth,2006(2):387-389. |
[5] | 张治安,杨邦朝,胡永达,邓梅根,汪斌华.纳米氧化锰电极材料的制备和电容特性研究[J].无机化学学报,2005(03):389-393. |
[6] | LEE H Y;GOODENOUGH J B .Supercapacitor behavior with KCI electrolyte[J].Journal of Solid State Chemistry,1999,144:220-223. |
[7] | REDDY R N;REDDY R G .Synthesis and electrochemical characterization of amorphous MnO2 electrochemical capacitor electrode material[J].Journal of Power Sources,2004,132:315-320. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%