在惰性气体保护的全封闭系统内,采用直流氢电弧蒸发-冷凝与放电等离子烧结相结合的技术制备出高致密度、晶粒尺寸细小且分布均匀的纯铝纳米晶块体材料.对制备材料的结构分析表明,铝纳米晶块体具有很高的纯度,纳米晶界面洁净无杂相.对制备的铝纳米晶块体的力学性能测试表明,其显微硬度为2.12GPa,比铝粗晶材料提高了约6倍;而弹性模量与粗晶块体相比变化不大.
参考文献
| [1] | X.L. Zhong;W.L.E. Wong;M. Gupta .Enhancing strength and ductility of magnesium by integrating it with aluminum nanoparticles[J].Acta materialia,2007(18):6338-6344. |
| [2] | 文玉华,周富信,刘曰武.纳米材料的研究进展[J].力学进展,2001(01):47-61. |
| [3] | 卢柯.纳米晶体Cu的室温超塑延展性[J].中国科学院院刊,2001(01):29-31. |
| [4] | Karimpoor AA;Aust KT;Erb U .Charpy impact energy of nanocrystalline and polycrystalline cobalt[J].Scripta materialia,2007(3):201-204. |
| [5] | SRINIVASARAO B;OH-ISHI K;OHKUBO T et al.Synthesis of high-strength bimodally grained iron by mechanical alloying and spark plasma sintering[J].Scripta Materialia,2008,1:1-4. |
| [6] | Song XY;Zhang JX;Yue M;Li ED;Zeng H;Lu ND;Zhou ML;Zuo TY .Technique for preparing ultrafine nanocrystalline bulk material of pure rare-earth metals[J].Advanced Materials,2006(9):1210-1215. |
| [7] | 贾冲;张喜燕;周世杰 .冷轧变形纳米晶钴的X射线衍射研究[J].功能材料,2007,38:3769-3772. |
| [8] | 谢佑卿,刘心笔.金属Al的电子结构和物理性质[J].中国科学E辑,1999(05):391-395. |
| [9] | 张久兴,刘科高,周美玲.放电等离子烧结技术的发展和应用[J].粉末冶金技术,2002(03):129-134. |
| [10] | 宋晓艳,刘雪梅,张久兴.放电等离子烧结中显微组织演变的自调节机制[J].中国体视学与图像分析,2004(03):140-146. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%