在工业实验中研究了低频电磁场对水平连铸奥氏体不锈钢组织的影响,结果表明:在低频电磁场作用下,合适的电磁搅拌参数使奥氏体不锈钢宏观组织在一定程度上得到了明显改善,铸坯的柱状晶和等轴晶得到了显著的细化,消除了穿晶现象,等轴晶区扩大,中心缩孔、中心疏松级别明显降低;多次实验发现:对于奥氏体不锈钢,所需的搅拌强度应高于一般钢种,即使搅拌器的中心磁感应强度达900GS平均值(幅值达到1413GS),采用3~4Hz的频率,搅拌后对钢液的组织影响较小;在同样的磁场强度下,不锈钢液由于粘度大,因而其转速比碳钢液的转速约低20%~30%.
参考文献
[1] | HEARD R.Renew of horizontal continuous casting technology[A].USA:Iron and Steel Society/AIME,1998:147-154. |
[2] | HAISSIG M .Horizontal continuous casting:a technology for the future[J].Iron & Steel Engineers,1984,61(06):65-71. |
[3] | Takehiko TOH;Eiichi TAKEUCHI;Masatake HOJO .Electromagnetic Control of Initial Solidification in Continuous Casting of Steel by Low Frequency Alternating Magnetic Field[J].ISIJ International,1997(11):1112-1119. |
[4] | Y.W.Cho .Mechanism of Surface Quality Improvement in Continuous Cast Slab with Rectangular Cold Crucible Mold[J].ISIJ International,1998(7):723-729. |
[5] | Anatoly F. KOLESNICHENKO;Anastasiya A. KOLESNICHENKO;Viktoriya V. BURYAK .Improvement of In-mold Electromagnetic Stirrer by Feeding of Magnetic System with Polyharmonic Current[J].ISIJ International,2004(2):342-349. |
[6] | 张宏丽,王恩刚,贾光霖,赫冀成.电磁搅拌提高铸坯等轴晶比率的数值模拟[J].东北大学学报(自然科学版),2001(05):535-538. |
[7] | 李庆春.铸件形成理论基础[M].北京:机械工业出版社,1982 |
[8] | Willers, B;Eckert, S;Michel, U;Haase, I;Zouhar, G .The columnar-to-equiaxed transition in Pb-Sn alloys affected by electromagnetically driven convection[J].Materials Science & Engineering. A, Structural Materials: Properties, Microstructure and Processing,2005(1-2):55-65. |
[9] | 齐雅丽,贾光霖,张国志.电磁搅拌对液态金属运动及凝固组织的影响[J].铸造技术,2005(02):118-120. |
[10] | 钟云波,孟宪俭,倪丹,任忠鸣,邓康,徐匡迪.旋转磁场净化钢液的实验研究[J].上海金属,2006(02):9-14. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%