研究Ti和C添加对Nd9.4Fe79.6B11合金磁性能的影响规律.结果表明:Ti和C联合添加能够在不降低合金剩磁的情况下显著提高合金的矫顽力,最佳工艺条件下制备出的Nd9.4Fe75.6Ti4B10.5C0.5合金薄带的剩磁Br=0.91T,矫顽力Hcj=975.6kA/m,磁能积(BH)max=135.4kJ/m3.在磁体密度为6.1g/cm3时,黏结Nd9.4Fe75.6Ti4B10.5C0.5磁体剩磁Br=0.68T,内禀矫顽力Hcj=975kA/m,最大磁能积(BH)max=78 kJ/m3,性能和MQ-D磁粉制备的黏结磁体性能相当,具有低价位高性能的特点.
参考文献
| [1] | MANAF A;BUCKLEY R A;DAVIES H A .New nanocrystalline high remanence Fe-Nd-B alloys by rapid solidification[J].Journal of Magnetism and Magnetic Materials,1993,128:307-310. |
| [2] | YANG S;LI S D;LIU X S et al.Exchange coupled Nd2Fe14B/ α-Fe nanocomposite magnets with fine α-Fe grains obtained by low wheel speed spinning[J].Journal of Alloys and Compounds,2002,343:217-220. |
| [3] | COEHOORN R;DEMOOIJ D B;DEWAARD C .Melt spun permanent magnet materials containing Fe3 B as the main phase[J].Journal of Magnetism and Magnetic Materials,1989,80:101-105. |
| [4] | S. Hirosawa;Y. Shigemoto;T. Miyoshi;H. Kanekiyo .Direct formation of Fe_3B/Nd_2Fe_(14)B nanocomposite permanent magnets in rapid solidification[J].Scripta materialia,2003(7):839-844. |
| [5] | YOU C Y;PING D H;HONO K .Magnetic properties and microstructure of Fe3 B/Pr14Fe14 B-type nanocomposite magnets with Co and Cr additions[J].Journal of Magnetism and Magnetic Materials,2006,299:136-144. |
| [6] | Zhongmin Chen;Y. Q. Wu;M. J. Kramer .A study on the role of Nb in melt-spun nanocrystalline Nd-Fe-B magnets[J].Journal of Magnetism and Magnetic Materials,2004(1/2):105-113. |
| [7] | 吴义生,倪建森,徐晖,王震,周邦新,黄照华.Nd10.1Fe（83.7-x-y）CoxZryB6.2永磁材料结构和磁性能的研究[J].中国稀土学报,2005(03):295-298. |
| [8] | HERBST J F .R2 Fe14 B materials.,intrinsic properties and technological aspects[J].Reviews of Modern Physics,1991,63(04):819-898. |
| [9] | Z. C. Wang;H. A. Davies;S. Z. Zhou .Effects of C content on the formation and magnetic properties of Nd_(2)Fe_(14)(BC)/α-Fe nanocomposite magnets[J].Journal of Applied Physics,2002(6):3769-3774. |
| [10] | Hayato Hashino;Yosuke Tazaki;Hiromitsu Ino .Effects of Zr and C additions on the magnetic properties and structures of melt-spun Fe_(83)Nd_(10)B_7-based nanocomposite magnets[J].Journal of Magnetism and Magnetic Materials,2004(1/2):68-75. |
| [11] | BRANAGAN D J;MCCALLUMN R W .Precipitation phenomenon in stoichiometric Nd2 Fe14 B alloys modified with titanium and titanium with carbon[J].Journal of Alloys and Compounds,1995,230:67-75. |
| [12] | W. C. Chang;D. Y. Chiou;S. H. Wu .High performance α-Fe/Nd(2)Fe↓(14) B-type nanocomposites[J].Applied physics letters,1998(1/6):121-123. |
| [13] | M. Daniil;H. Okumura;G. C. Hadjipanayis .Effect of carbon substitution on the magnetic properties of Nd-Fe-(B, C) nanocomposite magnets[J].Journal of Magnetism and Magnetic Materials,2003(3):316-324. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%