考察不同温度处理的聚酰亚胺前驱体凝胶膜的热稳定性和力学性能,以及不同升温速率对薄膜亚胺化程度的影响.结果表明:随着升温速率的增大,薄膜的亚胺化程度略有下降,但随着处理温度的升高,其热稳定性能和力学性能都有明显的提高,拉伸强度、弹性模量增大到107MPa和2770MPa.
参考文献
[1] | Smith C.H.;Turman B.N. .Insulations for metallic glasses in pulse power systems[J].IEEE Transactions on Electron Devices,1991(4):750-757. |
[2] | YU J.;SHIN T.J.;WANG X.;CAI W.;ZHOU D.;LEE K.-W. .Miscibility of Polyimide with Polymeric Primer and It s Influence on Adhesion of Polyimide to the Primed Copper Metal: Effect of Precursor Origin[J].Journal of Polymer Science, Part A. Polymer Chemistry,1999(19):2806-2814. |
[3] | Jung-ok Baek;Sun-joo Park;Hui-jin Gong;Wonho Kim .Polyurethane Modified Epoxy Adhesives for the Application to FCCL[J].Macromolecular symposia,2007(0):654-659. |
[4] | Ogawa T;Baba S;Fujii Y .Improvement of bond strength of BPDA-PDA-type polyimide film by corona discharge treatment[J].Journal of Applied Polymer Science,2006(4):3403-3408. |
[5] | FEGER C;KHOJASTEH M M;GRATH MC J E.Polyimides,materials,chemistry and characterization[M].New York:Elsevier,1988:363-369. |
[6] | BEYNEN E;ROGGEN J;VANHOOF R et al.High rate single substrate polymer etching for multi-chip-modules(MCM) and off-chip-interconnect applications[J].Microelectronic Engineering,1992,17(1-4):341-344. |
[7] | YONGSOK SEO;SANG MOOK LEE;DONG YOUNG KIM et al.Kinetic study of imidization of a poly(ester amic acid) by FT-Raman spectroscopy[J].Macromolecules,2005,21(05):149-155. |
[8] | 丁孟贤;何天白.聚酰亚胺新型材料[M].北京:科学出版社,1998:18-20. |
[9] | KREUZ J A;ENDREY A L;GAY F P et al.Studies of thermal cyclizations of polyamic acids and tertiary amine salts[J].Journal of Polymer Science Part A:Polymer Chemistry,1966,4(10):2607-2616. |
[10] | BRUCE A REINHARDT;FRED E ARNOLD .High-temperature reactive thermoplastic aromatic polyimides[J].Journal of Applied Polymer Science,1981,26:2679-2691. |
[11] | 焦健;雷渭媛.高聚物结构、性能与测试[M].北京:材料科学与工程出版中心,2003 |
[12] | 程茹,黄培,时钧.PA封端对ODPA/ODA聚酰亚胺薄膜热稳定性的影响[J].材料工程,2006(07):7-10. |
[13] | 黄培,耿洪斌,程茹,王晓东,时钧.长链聚酰胺酸的热环化动力学[J].高分子学报,2004(02):256-262. |
[14] | 来育梅,程茹,王晓东,黄培.热塑性聚酰亚胺热转变行为研究[J].材料工程,2006(09):6-9,13. |
[15] | 程茹,朱梦冰,孙琳,黄培.高温热处理对聚酰亚胺薄膜性能的影响[J].合成树脂及塑料,2007(01):40-42. |
[16] | 耿洪斌,黄培,时钧.聚酰胺酸在不同热处理过程中的热环化[J].高分子材料科学与工程,2005(03):192-195,200. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%