利用扫描电镜(SEM)、广角X射线衍射(WAXD)和小角X射线散射(SAXS)对200～275℃范围内逐步预氧化的聚丙烯腈纤维的断面形貌与微观结构进行了测试.根据各样品的WAXD,SAXS数据,分别计算了预氧化纤维的微晶尺寸、纤维内微孔大小、小孔洞所占的体积分数及微孔的分形维数,分析了材料的微观组织结构在预氧化过程中的变化.结果表明:随着预氧化温度的升高,纤维的微晶尺寸先增大后减小,纤维内微孔的尺寸先减小后增大,小孔洞所占的体积分数不断增大,微孔的分形维数先减小后增大.
参考文献
| [1] | Naito K;Tanaka Y;Yang JM;Kayawa Y .Tensile properties of ultrahigh strength PAN-based, ultrahigh modulus pitch-based and high ductility pitch-based carbon fibers[J].Carbon: An International Journal Sponsored by the American Carbon Society,2008(2):189-195. |
| [2] | Beatrice Lindsay;Marie-Laure Abel;John F.Watts .A study of electrochemically treated PAN based carbon fibres by IGC and XPS[J].Carbon: An International Journal Sponsored by the American Carbon Society,2007(12):2433-2444. |
| [3] | TZENG S;LIN Y .The role of electroless Ni-P coating in the catalytic graphitization of PAN-based carbon fibers[J].Carbon,2007,46(03):555-558. |
| [4] | 王秀飞,黄启忠,宁可焱,尹彩流,苏哲安,朱建军.硅化处理对炭纤维石墨化度的影响[J].材料工程,2007(01):52-55. |
| [5] | 乔小晶,于仁光,任慧,王长福.插层炭纤维与镀铜炭纤维的性能比较[J].材料工程,2004(07):47-50. |
| [6] | Zhang Wangxi;Liu Jie;Wu Gang .Evolution of structrue and properties of PAN precursors during their conversion to carbon fibers[J].Carbon: An International Journal Sponsored by the American Carbon Society,2003(14):2805-2812. |
| [7] | 张利珍,吕春祥,吕永根,吴刚平,贺福.聚丙烯腈纤维在预氧化过程中的结构和热性能转变[J].新型炭材料,2005(02):144-150. |
| [8] | 赵根祥;陈顺英 .PAN 纤维低温热氧化过程的结构变化[J].合成纤维工业,1999,22(02):13-16. |
| [9] | 张旺玺,刘杰,吴刚.聚丙烯腈原丝的预氧化[J].合成技术及应用,2003(04):23-30. |
| [10] | 何东新,王成国,王延相.聚丙烯腈原丝预氧化过程中的结构与性能变化[J].合成纤维工业,2004(03):33-36. |
| [11] | Meijie YU;Chengguo Wang;Yujun Bai .Influence of Precursor Properties on the Thermal Stabilization of Polyacrylonitrile Fibers[J].Polymer bulletin,2006(5):757-763. |
| [12] | 王延相,王成国,朱波,何东新,井敏,王强.聚丙烯腈基炭纤维制备过程中的表面形态和结构研究[J].新型炭材料,2005(01):51-57. |
| [13] | 李小佳,罗倩华,朱一钧,王海舟.聚丙烯腈基碳纤维预氧化过程[J].中国科学B辑,2001(01):72-77. |
| [14] | Mei-Jie YU;Cheng-Guo Wang;Yu-Jun Bai .SEM and OM Study on the Microstructure of Oxidative Stabilized Polyacrylonitrile Fibers[J].Polymer bulletin,2007(5/6):933-940. |
| [15] | 季敏霞,王成国.聚丙烯腈基碳纤维制备过程中微观结构的演变[J].材料导报,2007(05):111-114. |
| [16] | Miyoshi Kaburagi;Yuezhen Bin;Dan Zhu;Masaru Matsuo .Small angle x-ray scattering from voids within fibers during the stabilization and carbonization stages[J].Carbon: An International Journal Sponsored by the American Carbon Society,2003(5):915-926. |
| [17] | KATSUYA F;YASUTOSHI K;NAOTO K .Small-angle X-ray scattering study of the pore structure of carbon fibers prepared from a polymer blend of phenolic resin and polystyrene[J].Carbon,2001,39(02):287-324. |
| [18] | CHEREPANOY G P;BALANKIN A S;IVANOVA V S .Fractal fracture mechanics-a review[J].Engineering Fracture Mechanics,1995,51(06):997-1033. |
| [19] | 贺福.碳纤维及其应用技术[M].北京:化学工业出版社,2004:53. |
| [20] | 徐跃,李向山.炭纤维中纳米微孔的X射线小角散射分析[J].理化检验-物理分册,2003(01):28-31. |
| [21] | 陈宇晗,吴琪琳,潘鼎.不同纤维素原丝及其制备的炭纤维的分形比较[J].炭素,2006(03):19-23. |
| [22] | 徐仲榆;刘洪波;张红波.PAN石墨纤维的拉伸断裂机制[J].炭素技术,1993(02):21-23. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%