采用座滴法研究硅硼玻璃在分别具有FeO和FeO+Fe_3O_4氧化膜的可伐合金表面1000℃保温不同时间的润湿规律.用数码显微镜测量硅硼玻璃在可伐合金表面的接触角和润湿直径,用SEM研究晕圈的表面形貌以及玻璃和金属的截面形貌,并用能谱分析不同晕圈处的化学成分.结果表明:随着润湿时间的延长,玻璃在具有FeO和FeO+Fe_3O_4氧化膜的可伐合金表面的接触角不断减小并最终分别在25°和23°趋于稳定.可以观察到,在润湿过程中,熔融玻璃周围存在两个晕圈,可以根据接触角、晕圈和润湿直径的变化将润湿过程分成润湿初始期、润湿铺展期和润湿稳定期三个阶段.
The wettability of borosilicate glass on Kovar with oxides of FeO and FeO+Fe_3O_4 respec-tively was studied as a function of holding time at 1000℃ by the sessile drop method. The contact an-gle and drop diameter were measured by the VHX-100K digital microscopy. The surface micrographs of halo and cross-sections of glass and kovar were investigated by SEM, and the chemical composition of halos was studied by EDS analysis. The results show that the contact angle all decreases as the time increases, and the final contact angles are 25° and 23° for FeO and FeO+Fe_3O_4, respectively. Two halos are observed in the wetting process. By analyzing the change of contact angle, halo and drop di-ameter, wetting process could be divided into three stages: initial period, spreading period and equi-librium period.
参考文献
| [1] | Chern TS;Tsai HL .Wetting and sealing of interface between 7056 Glass and Kovar alloy[J].Materials Chemistry and Physics,2007(2/3):472-478. |
| [2] | 马英仁.封接玻璃（一）--对玻璃的要求及适于封接的金属[J].玻璃与搪瓷,1992(04):58. |
| [3] | Mantel M. .Effect of double oxide layer on metal-glass sealing[J].Journal of Non-Crystalline Solids: A Journal Devoted to Oxide, Halide, Chalcogenide and Metallic Glasses, Amorphous Semiconductors, Non-Crystalline Films, Glass-Ceramics and Glassy Composites,2000(1/3):294-301. |
| [4] | DONALD I W .Preparation,properties and chemistry of glassand glass-ceramic-to-metal seals and coatings[J].Journal of Materials Science,1993,28(11):2841-2886. |
| [5] | THOMAS W B II .Matched glass-to-metal seal improvements by controlled atmosphere metal oxidation[J].SOLID STATE TECHNOLOGY,1986,29(09):73-79. |
| [6] | BANDYOPADHYAY N;TAMHANKAR;SATISH S et al.Process conditions for hermetic sealing of Kovar to borosilicate glass[J].Adv Ceram,1989,26:597-604. |
| [7] | 陈建,顾明元,潘复生.活性金属/陶瓷粘着功[J].复合材料学报,2003(03):85-88. |
| [8] | LUO D W;SHEN Z S.Oxidation behavior of kovar alloy in controlling atmosphere[J].Acta Metallurgica Sinica Letter,2008 |
| [9] | 汪刚强;唐祥云;马莒生 .玻璃与氧化膜浸润性研究[J].功能材料,1995,26(04):371-373. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%