通过对直流电弧等离子体制备的Ni纳米颗粒钝化处理得到NiO包覆Ni纳米颗粒.并对试样的组成成分、形貌、晶体结构、粒度和氧化特性采用高分辨透射电子显微镜(HRTEM)、X射线衍射(XRD)、透射电子显微镜(TEM)和选区电子衍射(SAED)、热重和差示扫描量热分析仪(TGA/DSC)等手段进行分析.结果表明:经过表面钝化处理的NiO包覆Ni纳米颗粒具有明显的核-壳结构,内核为纳米Ni,外壳为NiO氧化物.颗粒呈球形,粒度均匀,分散性良好,粒径分布在20～70nm范围内,平均粒径为44nm,壳层氧化膜的厚度为5～8nm.壳核结构防止了纳米Ni颗粒的进一步氧化和团聚.
NiO encapsulated Ni nanoparticles were prepared by direct current arc plasma method and subsequently passivation.The chemical composition,morphology, crystal microstructure, particle size and oxidization resistance of the product were analyzed using the high-resolution transmission electron microscopy (HRTEM), X-ray diffraction (XRD), transmission electron microscopy (TEM) and the corresponding selected-area electron diffraction (SAED), thermogravimetric analyzer (TGA) and diffirential scanning calorimeter (DSC).The results showed that the NiO encapsulated Ni nanoparticles with clear core-shell structure.The core is consisted of particles of Ni,while the shell is consisted of NiO.The particle size of the samples was homogeneously distributed with spherical shape and well dispersed, the particle size distribution ranging from 20-70nm with the average particle size about 44nm and the thickness of the shell 5-8nm.The core-shell structure can prevent Ni nanoparticles from oxidation and agglomeration.
参考文献
| [1] | DRAVID V P;HOST J J;TENG M et al.Controlled-size nanocapsules[J].NATURE,1995,374(6523):602-605. |
| [2] | Bonard JM.;Wegrowe JE.;Jiao J.;Chatelain A.;Seraphin S. .Varying the size and magnetic properties of carbon-encapsulated cobalt particles[J].Chemical Physics Letters,2001(3-4):251-257. |
| [3] | Zhang ZD.;Skorvanek I.;Wen GH.;Kovac J.;Wang FW.;Yu JL. Li ZJ.;Dong XL.;Jin SR.;Liu W.;Zhang XX.;Zheng JG. .Shell/core structure and magnetic properties of carbon-coated Fe-Co(C) nanocapsules[J].Journal of Physics. Condensed Matter,2001(9):1921-1929. |
| [4] | X.L.Dong;Z.D.Zhang .Characterization of Fe-Ni(C) nanocapsules synthesized by arc discharge in methane[J].Journal of Materials Research,1999(5):1782-1790. |
| [5] | Z. H. Wang;Z. D. Zhang;C. J. Choi .Structure and magnetic properties of Fe(C) and Co(C) nanocapsules prepared by chemical vapor condensation[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,2003(1/2):289-293. |
| [6] | Zhang ZD.;Zheng JG.;Skorvanek I.;Kovac J.;Dong XL.;Li ZJ. Jin SR.;Yang HC.;Guo ZJ.;Liu W.;Zhuo XG.;Yu JL. .Structure and magnetic properties of boron-oxide-coated Fe(B) nanocapsules prepared by arc discharge in diborane - art. no. 024404[J].Physical Review.B.Condensed Matter,2001(2):4404-0. |
| [7] | MCHENRY M E;MAJETICH S A;ARTMAN J O et al.Superparamagnetism in carbon-coated Co particles produced by the kratschmer carbon arc process[J].Physical Review B,1994,49(16):11358-11363. |
| [8] | Song HH.;Chen XH. .Large-scale synthesis of carbon-encapsulated iron carbide nanoparticles by co-carbonization of durene with ferrocene[J].Chemical Physics Letters,2003(3-4):400-404. |
| [9] | Weize Wu;Zhenping Zhu;Zhenyu Liu;Yaing Xie;Jing Zhang;Tiandou Hu .Preparation of carbon-encapsulated iron carbide nanoparticles by an explosion method[J].Carbon: An International Journal Sponsored by the American Carbon Society,2003(2):317-321. |
| [10] | C. Baker;S. K. Hasanain;S. Ismat Shah .The magnetic behavior of iron oxide passivated iron nanoparticles[J].Journal of Applied Physics,2004(11):6657-6662. |
| [11] | JONES D E;BROUSSEAU P;FOUCHARD R C et al.Thermal characterization of passivated nanometer size aluminium powders[J].Journal of Thermal Analysis and Calorimetry,2000,61(03):805-818. |
| [12] | Kwon YS.;Gromov AA.;Ilyin AP.;Rim GH. .Passivation process for superfine aluminum powders obtained by electrical explosion of wires[J].Applied Surface Science: A Journal Devoted to the Properties of Interfaces in Relation to the Synthesis and Behaviour of Materials,2003(1/4):57-67. |
| [13] | PHUNG X;GROZA J;STACH E A et al.Surface characterization of metal nanoparticles[J].Materials Science and Engineering A:Structural Materials Properties Microstructure and Processing,2003,359(1-2):261-268. |
| [14] | KATZ J L;MIQUEL P F .Synthesis and applications of oxides and mixed oxides produced by a flame process[J].Nano-Structured Materials,1994,4(05):551. |
| [15] | Hong Bi;Shandong Li;Yuchuan Zhang .Ferromagnetic-like behavior of ultrafine NiO nanocrystallites[J].Journal of Magnetism and Magnetic Materials,2004(3):363-367. |
| [16] | ICHIYANAGI Y;WAKABAYASHI N;YAMAZAKI J et al.Magnetic properties of NiO nanopardcles[J].Physical Review B:Condensed Matter,2003,329-333(02):862-863. |
| [17] | L. Xiang;X. Y. Deng;Y. Jin .Experimental study on synthesis of NiO nano-particles[J].Scripta materialia,2002(4):219-224. |
| [18] | WEI Z Q;XIA T D;MA J et al.Efficient preparation for Ni nanopowders by anodic arc plasma[J].Materials Letters,2006,60(03):766-77. |
| [19] | KAITO C .Coalescence growth mechanism of smoke particles[J].Japanese Journal of Applied Physics,1985,24(03):261-264. |
| [20] | PABLO M;MICHAEL F .Particle aggregation with simultaneous surface growth[J].Physical Review E,2003,67(06):061407-061417. |
| [21] | BALL P;GARWIN L .Scanning tunneling microscopy and spectroscopy studies of nanostructured materials[J].Nature,1992,355(6363):761-764. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%