采用溶胶-凝胶法,以γ-甲基丙烯酰氧丙基三甲氧基硅烷(KH570)改性正硅酸乙酯(TEOS)水解聚合物,在钢片上制备有机-无机复合防腐薄膜.通过傅里叶红外光谱(FTIR)、扫描电镜(SEM)等测试手段研究薄膜材料的结构,并通过盐雾腐蚀试验和电化学阻抗谱测试对复合薄膜的防腐蚀性能进行检测,并探讨了最适加水量(R).结果表明:随R从1增加至5,涂层防腐性能先提高后降低.R=3时,薄膜结构致密,抗腐蚀性能最好;FTIR结果表明,样品经180℃热处理后,KH570的结构无明显变化.
参考文献
| [1] | V. Subramanian;W.J. Van .Silane based metal pretreatments as alternatives to chromating[J].Surface Engineering,1999(2):168-172. |
| [2] | Tang N.;Gorecki G.;Vanooij WJ. .COMPARATIVE EIS STUDY OF PRETREATMENT PERFORMANCE IN COATED METALS [Review][J].Progress in Organic Coatings: An International Review Journal,1997(4):255-263. |
| [3] | Sundararajan G.P.;Ooij W.J. .SILANE BASED PRETREATMENTS FOR AUTOMOTIVE STEELS[J].Surface Engineering,2000(4):315-320. |
| [4] | Zhu DQ.;van Ooij WJ. .Corrosion protection of metals by water-based silane mixtures of bis-[trimethoxysilylpropyl]amine and vinyltriacetoxysilane [Review][J].Progress in Organic Coatings: An International Review Journal,2004(1):42-53. |
| [5] | Danqing Zhu;Wim J. van Ooij .Enhanced corrosion resistance of AA 2024-T3 and hot-dip galvanized steel using a mixture of bis-[triethoxysilylpropyl]tetrasulfide and bis-[trimethoxysilylpropyl]amine[J].Electrochimica Acta,2004(7):1113-1125. |
| [6] | W. J. Van Ooij;D. Q. Zhu .SILANE BASED CHROMATE REPLACEMENTS FOR CORROSION CONTROL, PAINT ADHESION, AND RUBBER BONDING[J].Surface Engineering,2000(5):386-396. |
| [7] | VAN OOIJ W J;CHILD T .Protecting metals with silane coupling agents[J].Chemtech,1998,28(02):26-35. |
| [8] | VAN OOIJ W J .Metal preteated with an aqueous solution containing a dissolved inorganic silicate or aluminate,organofunctional and a nonfunctional silane for enhance corrosion resistance[P].USA Patent:5,433,976,1995-07-18. |
| [9] | VAN OOU W J .Metal substrate with enhanced corrosion resistance and improved paint adhension[P].USA Patent:5,455,080,1995-10-03. |
| [10] | VAN OOIJ W J .Metal substrate with enhanced corrosion resistance and improved paint adhension[P].USA Patent:5,539,03 1,1996-07-23. |
| [11] | T.F. Child;W.J. Van .Application of silane technology to prevent corrosion of metals and improve paint adhesion[J].Transactions of the Institute of Metal Finishing,1999(3):64-70. |
| [12] | 尤宏,刘琰,孙德智,胡立江.LY12铝合金表面有机-无机杂化膜的防腐性能研究[J].材料工程,2004(06):7-11. |
| [13] | Liu Y;Sun DZ;You H;Chung JS .Corrosion resistance properties of organic-inorganic hybrid coatings on 2024 aluminum alloy[J].Applied Surface Science: A Journal Devoted to the Properties of Interfaces in Relation to the Synthesis and Behaviour of Materials,2005(1/3):82-89. |
| [14] | Zandi-zand R;Ershad-langroudi A;Rahimi A .Silica based organic-inorganic hybrid nanocomposite coatings for corrosion protection[J].Progress in Organic Coatings: An International Review Journal,2005(4):286-291. |
| [15] | Zandi-zand R;Ershad-langroudi A;Rahimi A .Organic-inorganic hybrid coatings for corrosion protection of 1050 aluminum alloy[J].Journal of Non-Crystalline Solids: A Journal Devoted to Oxide, Halide, Chalcogenide and Metallic Glasses, Amorphous Semiconductors, Non-Crystalline Films, Glass-Ceramics and Glassy Composites,2005(14/15):1307-1311. |
| [16] | POPPE ANDREAS;WESTHOFF ELKE;STUBBE WILFRIED .Epoxy functional silanes.methods for the production thereof and use of the same[P].Germany:WO2004/099220,2004-04-23. |
| [17] | 化学工业时报[M].东京:化学工业时报社,1994 |
| [18] | 王楠,徐溢,杨立华,滕毅.硅烷试剂防腐蚀工艺研究[J].材料保护,2001(11):32-33. |
| [19] | 赖琛 .耐高温防腐蚀涂料的研制[D].湖南大学,2002. |
| [20] | 尹志岚,袁媛,刘昌胜.硅烷偶联剂对不锈钢表面膜基结合强度的影响[J].功能高分子学报,2004(02):298-302,306. |
| [21] | DAVIS P J;BRINKER C J;SMITH D M .Pore structure evolu-tion in silica gel during aging/drying.I:temporal and thermal aging[J].Journal of Non-Crystalline Solids,1992,142(03):189-196. |
| [22] | GE Man-zhen;YANG Hui;DING Zi-shang.Polysilicates sructure and coating characte ristics[J].Bulletin of the Chinese Ceramie Society,1994(05):32-36. |
| [23] | ZHANG Z Y;WAKABAYASHI H .Structural study of Al(acac)3 catalyzed CH3SiO3/2 gel[J].Journal of Sol-Gel Science and Technology,1998,12:153-158. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%