通过蠕变曲线测定及组织形貌观察,研究了一种9％W单晶镍基合金的组织演化与蠕变行为.结果表明,当在1040℃施加应力大于160MPa时,合金表现出明显的施加应力敏感性,在试验的温度范围内,合金具有较低的应变速率和较长的蠕变寿命,测定出合金的表观蠕变激活能为465kJ/mol.在蠕变初期,合金中γ'相沿垂直于应力轴方向,转变成N-型筏状结构,在稳态蠕变期间合金的变形机制是位错攀移越过筏状γ'相,而蠕变后期合金的变形机制是位错剪切进入筏状γ'相.蠕变断裂后,在试样不同区域筏状γ'相具有不同的形貌,在远离断口区域,筏状γ'相与应力轴方向垂直,而在近断口区域筏状γ'相尺寸及扭曲程度增加的原因是承受的应力及变形程度增大所致.
参考文献
| [1] | 胡壮麒,刘丽荣,金涛,孙晓峰.镍基单晶高温合金的发展[J].航空发动机,2005(03):1-7. |
| [2] | Luo ZP.;Wu ZT.;Miller DJ. .The dislocation microstructure of a nickel-base single-crystal superalloy after tensile fracture[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2003(1/2):358-368. |
| [3] | NYSTROMJD;POLLCKTM;MURPHYWH et al.Discontinuous cellular precipitation in a high-refractory nickel-base supcralloy[J].Metall Mater Trans (A),1997,28:2443-2450. |
| [4] | YU X H;YRO Y Y.Design of quaternary Ir-Nb-Ni-Al refractory supcralloys[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,2000(31):173-181. |
| [5] | Luo ZP.;Wu ZT.;Miller DJ. .The dislocation microstructure of a nickel-base single-crystal superalloy after tensile fracture[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2003(1/2):358-368. |
| [6] | 王开国,李嘉荣,曹春晓.单晶高温合金蠕变行为研究现状[J].材料工程,2004(01):3-7,11. |
| [7] | NATHAL M V;EBERT L J.The Influence of Cobalt,Tantalum,and Tungsten on the Microstructure of Single Crystal Nickel-Base Superalloys[J].Metallurgical and Materials Transactions,1985(16A):1849-1862. |
| [8] | 阳大云,张炫,金涛,孙晓峰,管恒荣,胡壮麒.钴、钨和钛对镍基单晶高温合金持久性能的影响[J].稀有金属材料与工程,2005(08):1295-1298. |
| [9] | MUKHERJEE A.K;BIRD J.E;DORN J.E .Experimental correlation for high-temperature creep[J].Transactions ASM,1969,62:155-166. |
| [10] | KEARSEY R M;BEDDOES J C;JAANSALU K M.The effects of Re,W and Ru on microsegregation behaviour in single crystal superalloy[A].United States:Metals and Materials Society,2004:801-810. |
| [11] | ZHANCJ H;HUZQ;XU Y B et al.Dislocation structure in a single crystal nickel-base superalloy during low cycle fatigue[J].Metall Trans (A),1992,23:1253-1258. |
| [12] | GABR1SCH H;MUKHERJI D;WAHI R P .Deformation induced dislocation networks at the γ/γ' interfaces in the single crystal superalloy[J].Philosophical Magazine,1996,A74(01):229-241. |
| [13] | GABB T P;DRAPER S L;HULL D R .The role of interfacial dislocation networks in high temperature creep of superalloys[J].Materials Science and Engineering,1989,A118(03):59-69. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%