利用高温高压反应釜模拟高含硫气田H2S/CO2共存环境,在流动溶液介质中进行腐蚀实验,辅以SEM和XRD,探讨了温度对API-X60管线钢H2S/CO2腐蚀行为的影响.结果表明:随温度的升高X60钢的腐蚀速率先升高后降低,腐蚀形态由局部腐蚀趋于全面腐蚀,高温区有点蚀倾向.低温区形成的腐蚀产物以马基诺矿型晶体(FeS1-X)和FeS单硫化物为主,随温度升高腐蚀产物以层片状马基诺矿型晶体为主,并出现少量磁黄铁矿型(Fe1-XS)晶体;高温区则以磁黄铁矿型晶体为主.低温区腐蚀产物附着力差导致其覆盖率降低,膜层脱落处的阳极反应速率由于膜层覆盖处的阴极效应而加快,使点蚀迅速发展.
参考文献
| [1] | SMITH S N;PACHECO J L.Prediction of corrosion in slightly sour environments[A].Houston:NACE,2002 |
| [2] | ABAYARATHNA D;NARAGHI A;WANG S H.The effect of surface films on corrosion of carbon steel in a CO2-H2S-H2O system[A].Houston:NACE,2005 |
| [3] | Li, Y;van Santen, RA;Weber, T .High-temperature FeS-FeS2 solid-state transitions: Reactions of solid mackinawite with gaseous H2S[J].Journal of Solid State Chemistry,2008(11):3151-3162. |
| [4] | J.L. Mora-Mendoza;J.G. Chacon-Nava;G. Zavala-Olivares .Influence of Turbulent Flow on the Localized Corrosion Process of Mild Steel with Inhibited Aqueous Carbon Dioxide Systems[J].Corrosion: The Journal of Science and Engineering,2002(7):608-619. |
| [5] | 刘烈炜,张振飞,徐东林.抗硫碳钢在高温高压CO2/H2S条件下腐蚀速率的研究[J].材料保护,2008(01):15-16,50. |
| [6] | 朱世东,刘会,白真权,林冠发,尹成先.模拟油田CO2/H2S环境中P110钢的动态腐蚀行为[J].石油与天然气化工,2009(01):65-68. |
| [7] | 田伟,谢发勤,严密林,周卫军.温度对80SS油管钢腐蚀行为的影响[J].电镀与环保,2008(01):34-37. |
| [8] | 张清,李全安,文九巴,白真权.温度对油管钢CO2/H2S腐蚀速率的影响[J].材料保护,2004(04):38-39. |
| [9] | 张清,李全安,文九巴,白真权.温度和压力对N80钢CO2/H2S腐蚀速率的影响[J].石油矿场机械,2004(03):42-44. |
| [10] | 姜放,戴海黔,曹小燕,黄红兵.油套管在CO2和H2S共存时的腐蚀机理研究[J].石油与天然气化工,2005(03):213-215. |
| [11] | 李国敏,刘烈伟,郑家燊.碳钢在含硫化氢及高压二氧化碳饱和的NaCl溶液中的腐蚀行为[J].中国腐蚀与防护学报,2000(04):204-210. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%