采用超声疲劳试验方法和试样尺寸相近的高频疲劳试验方法对S06钢进行疲劳性能试验,将试验数据和试样断口形貌进行对比,研究超声疲劳试验方法对S06钢疲劳性能和裂纹萌生机制的影响.结果表明:在相同的应力水平下,超声加载频率下S06钢的疲劳寿命高于高频疲劳试验测得的疲劳寿命;超声疲劳试验中裂纹全部从表面萌生,而高频疲劳试样裂纹有表面萌生和内部萌生两种机制.分析了超声加载频率对S06钢疲劳性能和裂纹萌生机制产生影响的原因:对疲劳性能的影响与金属材料的晶体结构和裂纹尖端的化学反应有关,对裂纹萌生机制的影响与试样表层残余应力松弛有关.
参考文献
[1] | C. Bathias .Piezoelectric fatigue testing machines and devices[J].International Journal of Fatigue,2006(11):1438-1445. |
[2] | 闫桂玲,王弘,高庆.超声疲劳试验方法及其应用[J].力学与实践,2004(06):25-29. |
[3] | H. Mayer;M. Papakyriacou;R. Pippan;S. Stanzl-Tschegg .Influence of loading frequency on the high cycle fatigue properties of AlZnMgCu1.5 aluminium alloy[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2001(1/2):48-54. |
[4] | 王弘,高庆.超声疲劳试验中载荷频率对材料疲劳性能的影响[J].理化检验-物理分册,2005(09):433-435,455. |
[5] | Y. Akiniwa;N. Miyamoto;H. Tsuru .Notch effect on fatigue strength reduction of bearing steel in the very high cycle regime[J].International Journal of Fatigue,2006(11):1555-1565. |
[6] | Yu-kui Gao;Mei Yao;Pei-ge Shao .Another Mechanism for Fatigue Strength Improvement of Metallic Parts by Shot Peening[J].Journal of Materials Engineering and Performance,2003(5):507-511. |
[7] | 高玉魁.超高强度钢喷丸表面残余应力在疲劳过程中的松弛规律[J].材料热处理学报,2007(z1):102-105. |
[8] | 韩冬,谭明华,王伟明,何闻.振动时效技术的研究及发展[J].机床与液压,2007(07):225-228,244. |
[9] | B. Zettl;H. Mayer;C. Ede .Very high cycle fatigue of normalized carbon steels[J].International Journal of Fatigue,2006(11):1583-1589. |
[10] | R. Ebara .The present situation and future problems in ultrasonic fatigue testing - Mainly reviewed on environmental effects and materials' screening[J].International Journal of Fatigue,2006(11):1465-1470. |
[11] | Ryan J. Morrissey;Theodore Nicholas .Fatigue strength of Ti-6Al-4V at very long lives[J].International Journal of Fatigue,2005(10/12):1608-1612. |
[12] | H. Mayer;M. Papakyriacou;B. Zettl .Influence of porosity on the fatigue limit of die cast magnesium and aluminium alloys[J].International Journal of Fatigue,2003(3):245-256. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%