通过实验室退火与回火,采用力学测定与显微组织分析研究了马氏体体积分数与回火温度对双相钢屈服特性的影响.结果表明:随马氏体体积分数从0%增加到约15%,双相钢的屈服强度显著降低,降低值约为80～100MPa;而马氏体体积分数在15%～35%之间,双相钢的屈服强度维持在一个较低的水平.当马氏体体积分数大于35%,双相钢屈服强度急剧上升.当马氏体体积分数超过10%,双相钢表现为连续屈服.随回火温度从200℃升高到400℃,双相钢的屈服强度单调增加.回火温度大于300℃,双相钢重新出现物理屈服平台.对双相钢精细显微结构的观察分析得出,铁素体中的高密度相变诱发位错及残余应力是导致双相钢低屈服强度与连续屈服的可能原因.
参考文献
| [1] | BHATTACHARYA D.Developments in advanced high strength steels[A].北京:冶金工业出版社,2006:70-73. |
| [2] | Rocha RO;Melo TMF;Pereloma E;Santos DB .Microstructural evolution at the initial stages of continuous annealing of cold rolled dual-phase steel[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2005(1/2):296-304. |
| [3] | ERDOGAN M .Effect of austenite dispersion on phase transformation in dual phase steel[J].Scripta Materialia,2003,48(05):501-506. |
| [4] | Mehmet Erdogan;Suleyman Tekeli .The effect of martensite volume fraction and particle size on the tensile properties of a surface-carburized AISI 8620 steel with a dual-phase core microstructure[J].Materials Characterization,2002(5):445-454. |
| [5] | 蒋俊华,李俊,胡文彬.超高强低碳Si-Mn冷轧双相钢的回火组织和力学性能研究[J].金属热处理,2007(09):14-18. |
| [6] | 花礼先;王绪 .连续退火冷轧双相钢板的屈服点延伸[J].北京科技大学学报（自然科学版）,1993,15(02):155-158. |
| [7] | 徐祖耀.马氏体相变和马氏体[M].北京:科学出版社,1980:87. |
| [8] | 马鸣图;吴宝榕.双相钢--物理和力学冶金[M].北京:冶金工业出版社,2009 |
| [9] | 张丙;冯锋;万晓景 .低碳合金双相钢低温时效机理探讨[J].金属热处理学报,1994,15(02):7-12. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%